Abstract:Machinable zirconia blocks with gradient colors are fundamental for fabrication of full-contour esthetic dental restorations. The aim of this study was to process and evaluate bi-colored zirconia ceramics as a pilot dental material by using well-established techniques. Two commercially available partially stabilized zirconia granules, one undoped and one doped with 0.202wt% Fe2O3, resulted in white and yellow colors after sintering, respectively. Bi-colored zirconia was fabricated by two-step dry pressing of both zirconia granules one above the other to form green bodies, followed by cold isostatic pressing (CIP) and, a two-step pressureless sintering finally at 1450°C. The dilatometer results showed that the Fe2O3 doped zirconia sintered slightly rapid, but the difference of shrinkage between two powders was <1%. Sintered bars achieved full density, 6.018g/cm3 (∼99%TD), without cracks in the ∼1mm color gradient zone. The microstructures were characterized by scanning electron microscopy (SEM) and careful observation of both surface and interior provided no obvious structural difference of either grains or pores among the three distinct regions, comprising white, yellow and color gradient zone. Vickers hardness of bi-colored zirconia was ∼13.1GPa, with no obvious difference in the three regions. The four-point bending strength of the bi-colored zirconia bars was 745.5±159.6MPa, which appeared noticeably lower than that of the single-colored references being above 1000MPa. Fractographic analysis revealed that in most of the cases (60%) the fracture was initiated at the color gradient zone, where large voids with high coordination numbers, agglomerates with critical size and concentration of irregular grains with porous surfaces were observed. Above all, bi-colored zirconia ceramics prepared by the improved technique could meet the basic requirements of dental materials. The ways of minimizing the defects within bi-colored blocks should be developed for the production of esthetic zirconia ceramics of high strength and reliability.

Fabrication of Colored Dental Yttria-Stabilized Tetragonal Zirconia Polycrystal via Heterogeneous Precipitation Method

Research on the Coloration of Dental Zirconia

Preparation of Black-Colored Zirconia Ceramics via Heterogeneous Precipitation

The Color of Fe<sub>2</sub>O<sub>3</sub> and Bi<sub>2</sub>O<sub>3</sub> Pigmented Dental Zirconia Ceramic

Effect of Pigmentation on the Mechanical Properties and Microstructure of Dental 3Y-TZP Ceramics

Production and properties of tooth-colored yttria stabilized zirconia ceramics for dental applications

Conventional sintering of nano-crystalline Yttria-Stabilized Zirconia enables high-strength, highly translucent and opalescent dental ceramics

Fabrication of Colored Zirconia Ceramics Doped with the Spinelvia Heterogeneous Nucleation Method

Bi-colored zirconia as dental restoration ceramics

Production and characterization of self-colored dental zirconia blocks

Color Reproduction And Shade Stability Of Zirconia Ceramics

Preparation and Properties of Dental Zirconia Ceramics

Study of colored on the microwave sintering behavior of dental zirconia ceramics

Synthesis of Coloured Dental Zirconia Ceramics and Their Mechanical Behaviors

Acquisition of locational information about reference points during blindfolded and sighted locomotion: effects of a concurrent task and locomotion paths.

Fabrication of Blue-Colored Zirconia Ceramics via Heterogeneous Nucleation Method

One-step hydrothermal synthesis of yttria-stabilized tetragonal zirconia polycrystalline nanopowders for blue-colored zirconia-cobalt aluminate spinel composite ceramics

Preparation and properties of black Ti-doped zirconia ceramics

Fabrication of Coloured Zirconia Ceramics by Infiltrating Water Debound Injection Moulded Green Body

Critical evaluations on the crystallographic properties of translucent dental zirconia ceramics stabilized with 3-6 mol% yttria

In vitro evaluation of tooth-colored yttria stabilized zirconia ceramics