Preparation of Black-Colored Zirconia Ceramics via Heterogeneous Precipitation

千粉玲,谢志鹏,孙加林,王峰
DOI: https://doi.org/CNKI:11-2310/TQ.20110726.1521.012
2011-01-01
Abstract:A heterogeneous precipitation method was introduced to fabricate coloring agent/zirconia composite powder and then black-colored zirconia ceramic was obtained after shaping and sintering when Y-TZP(yttria-stabilized tetragonal polycrystals zirconia) was used as starting materials,manganese and aluminum nitrates as coloring agent and PEG 2000 as dispersant.The X-ray diffraction,scanning electron microscope,X-ray fluorescence and transmission electron microscope were used to characterize the microstructure and properties of composite powders and ceramics.It was found that the prepared composite powder has a shell–core structure and the fabricated zirconia ceramic appears bright black with homogeneous,fine and dense microstructure after sintering.The faceted MnAl2O4 grains were uniformly dispersed in zirconia matrix.Compared to conventional mechanical mixing method,the mass trans-ferring distance for the reaction of the incorporated colorant elements could be effectively reduced when a heterogeneous precipitation method was used,which could facilitate the formation of coloring phases with less volatilization.It was,therefore,believed that the heterogeneous precipitation method could be a novel and cost-saving route for the fabrication of black zirconia ceramic.
What problem does this paper attempt to address?