The Impact of ZnO on Structure and Optical Performances for TeO2-Nb2O5 Glass

林健,黄文旵,朱小蓉,江丽,孙真荣

DOI: https://doi.org/10.3321/j.issn:1001-9731.2003.06.037

2003-01-01

Journal of Functional Biomaterials

Abstract:TeO_2-Nb_2O_5 glass was a new kind of heavy metal oxide glass with excellent nonlinear optical performances. The optical transmittance, nonlinear optical performance and structure of the glass were investigated as function of ZnO content. The nonlinear optical performances of the glass, arising from electron cloud deformation, could be improved by adding few ZnO content. The third-order nonlinear optical susceptibility (_χ_~((3))) as measured by a degenerate four wave mixing (DFWM) method, initially increased with increasing ZnO content to about 9.2×10~(-13)esu for a glass containing 2.5wt% ZnO, and then down to 6.0×10~(-13)esu with increasing ZnO content up to 10wt%. The _χ_~((3)) value had no significantly changes in the ZnO content range from 10wt% to 15wt%. The transmittance of the glass could be improved by adding 15wt% ZnO. The structure of these glasses as analyzed by Raman spectroscopy, was affected by the addition of ZnO content up to 5wt%. It was believed that the Zn~(2+) ions would occupy the interstitial of the glass network by replacing the Nb~(5+) ions, and ZnO content provide with more free oxygen ions. Therefore, the exceed ZnO content could make ~(4-) transfer into ~(2-) group in the glass network.