Pure TeO 2 glass: Influence of synthesis conditions on linear and non-linear optical, magneto-optical and structural properties
J. Hrabovsky,N.S. Tagiara,J. Mistrik,L. Strizik,P. Rysanek,V. Kopecky Jr.,J. Kozlik,J. Orava,S. Wang,T. Ishibashi,E.I. Kamitsos,M. Veis
DOI: https://doi.org/10.1016/j.jallcom.2024.174788
IF: 6.2
2024-05-18
Journal of Alloys and Compounds
Abstract:The first systematic study of linear and non-linear optical, magneto-optical and structural properties of pure TeO 2 glass is presented with regard to different synthesis and material processing conditions. Prepared glasses were synthesized by the intermittent quenching from 900 ∘ C in platinum or alumina crucibles and characterized prior to and after optical polishing. The position of the long-wavelength/phonon absorption edge was investigated using various optical models and experimentally obtained data of refractive index and Verdet constants were used for the estimation of magneto-optical anomaly parameter. During synthesis in alumina crucible, up to about 11 wt.% of Al 2 O 3 incorporates into the glass (verified by EDS/XRF and Raman/FTIR spectroscopy) partially transforming the original pure TeO 2 glass backbone structure composed of [TeO 4 ] trigonal bipyramids to [TeO 3+1 ] and [TeO 3 ] structural units with the expected integration of Al into Te − O − Al bridges. The presence of Al 2 O 3 results in lowered density ρ (5.60 → 4.72 g cm −3 ), refractive index n 1550 (2.086 → 1.927) and Verdet constant V 632 (36.3 → 21.9 rad T −1 m −1 ) and in increased optical-band-gap energy E g (3.69 → 3.72 eV) and Abbe number ν D (19.9 → 26.9) compared to pure TeO 2 glass prepared in platinum crucible. A dataset of the obtained complex optical parameters (refractive index and extinction coefficient) in the wide spectral range of 193 − 11000 nm is included in the supplementary part.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering