A New Way to Prepare Some Supported Catalysts with Highly Specific Surfaces
Zhao Biying,Xu Xianping,Ma Huarong,Gao Jinming,Wang Rongqiu,Sun Donghong,Tang Youqi
DOI: https://doi.org/10.3866/pku.whxb19930103
1993-01-01
Acta Physico-Chimica Sinica
Abstract:In this paper, a new way to increase the specific surface areas of supported catalysts has been suggested. The results for MoO3/ZrO2, WO3/ZrO2, CuO/ZrO2, SO42-/ZrO3, NiO/ZrO2, Fe2O3/ZrO2, Fe-2(SO4)(3)/ZrO2, MoO3/TiO2, SO42-/TiO2, NiSO4/TiO2, V2O5/TiO2 etc. system show that the specific surfaces areas of the samples, prepared by impregnating some hydoxides then calcinating at high temperature, are much larger than those of the samples prepared with a traditional method-impregnating their oxides calcinated at the same temperature. Using this way, the specific surface areas of some supported catalysts can increase by serveral times. The surface areas of some supports such as zirconia and titania are not large enough, and they are easy to sinter at high temperature. In these cases, the advantage of this preparation method is fully displayed, and the specific surface areas of the resulting zirconia - or titania - supported catalysts can compare favourably with those of the catalysts prepared from some classical supports (such as gamma-Al2O3, SiO2).In addition, it has been proved by means of XPS, XRD, LRS and DTA that as an active component disperse on a support as a monolayer and its content comes up to its monolayer dispersion capacity, the specific surface area of the obtained catalyst would be the largest. We suggest a mechanism that an active component covered on a support can not only segregate its particles, but also hinder the surface diffusion of support, and as a result, its crystalline growth, an accompanying phase transformation and inter-crystalline sintering are all retarded.