Abstract:The C=C double bonds in the main chain of hydroxyl-terminated polybutadiene (DHTPB), obtained by the degradation of polybutadiene rubber, were partially epoxided using m-chloroperoxybenzoic acid (mCPBA) as epoxidation reagent. A series of epoxided HTPBs (EHTPB) with different epoxy contents (5%, 10% and 15%) were prepared by tuning the molar ratio of mCPBA to C=C double bonds. The structures of EHTPBs were characterized by Fourier transform-infrared (FTIR), nuclear magnetic resonance (H-1-NMR) spectroscopy and gel permeation chromatography (GPC). The epoxy percent in EHTPBs from H-1-NMR spectra was in accordance with the design. In addition, a series of EHTPB-based polyurethane elastomers (EPU) were prepared by the reaction between EHTPB and 4,4'-diphenylmethane diisocyanate with 1,4-butanediol as a chain extender. Mechanical and thermal properties of the EPU samples were characterized by tensile test, differential scanning calorimetry (DSC) and thermal gravity analysis (TGA). With increased epoxy percent in EHTPB, the Young's modulus and the tensile strength of the EPU samples increased, whereas the elongation at break decreased. The sample EPU10 prepared with 10% of epoxy had the best mechanical properties with 8.82 MPa as Young's modulus, 7.83 MPa as tensile strength, and (485 +/- 23)% as elongation at break. The elasticity recovery of the EPU sample was slightly better than HTPB-based PU (EPU0). The results with TGA test showed that the thermal degradation of EPU, similar to EPU0, was divided into three stages. However, the EPU samples had better thermal stability with the initial degradation temperature at 210 degrees C, about 30 degrees C higher than that of EPU0. The DSC results showed that the glass transition temperature (T-g) of EPU gradually increased as epoxy percent was increased, though still lower than that of HTPB (FHTPB) based PUs prepared by free-radical polymerization.

Discussion on Preparation of High Solid Moisture Cured Polyurethane Elastomer

Preparation and Properties of Epoxided Hydroxyl-terminated Polybutadiene Based Polyurethane Elastomers

Preparation and Properties of Polyurethane/Montmorillonite Nanocomposites Cured under Room Temperature

Optimal Preparation and Characterization of Poly(urea–formaldehyde) Microcapsules

Influence of preparation method on adhesion and drying performances of polyurethane dispersion

Study on the Properties of Polyurethane–Urea Elastomers Prepared by TDI/MDI Mixture

Design, Preparation and Properties of Polyurethane Dispersions via Prepolymer Method

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Preparation and Characterization of Graft Copolymer EVA-g-PU

Preparation and Surface Properties of Silicone-Modified Polyester-Based Polyurethane Coats

Preparation and properties study of waterborne polyurethane synthesized by mixing polyester diols and isocyanates

Preparation and Characterization of Silicone Oil Modified Polyurethane Damping Materials

Preparation, mechanical properties of waterborne polyurethane and crosslinked polyurethane‐acrylate composite

Preparation and Properties of Silicone-Acrylate Copolymer Latex

Preparation and Characterization of Polyaspartic and a High Solids Acrylic Copolymer Polyol Based Polyurethanes

Preparation and properties of polyester diol and waterborne polyurethane

A novel strategy for preparation of solvent-free high-solid content water-based polyurethane

Preparation and Properties of Advanced Materials for Bi-component Polyurethane Adhesives Containing Siloxane.

Study on Preparation and Performance of Reactive Polyurethane Hot Melt Adhesives Based on a Polycarbonate Diol and a Polyester Diol

Preparation and characterization of high solid content cationic waterborne polyurethane with core‐shell structures

Preparation and properties of block copolymerization thermoset polyurethane elastomers prepared in situ