Abstract:<p>With increasing desires to protect the environment, volatile organic solvent emissions have been restricted, and there is a trend in developing waterborne polyurethanes. However, poor water resistance and low mechanical strength of waterborne polyurethane are major obstacles. Herein, we propose a terpene-modified polysiloxane-based polyurethane that solves the above-stated problems. In the presence of the Karstedt catalyst, isobornyl acrylate (IBOA) was introduced into the branch of hydrogen-containing silicone oil (HSO) through the hydrosilylation reaction. Then, it was mixed with an alkaline aqueous solution to convert the remaining SiH bonds to Si−OH bonds, which can be used as a polyol component (IBOA-Si-OH). Then, the mixtures of IBOA-Si-OH and polypropylene glycol-400 (PPG-400) were used as polyol components to react with polyisocyanate-3100 (PI-3100) in preparing a two-component waterborne polyurethane. Compared with the unmodified polyurethane film, the contact angle of the polyurethane film modified with IBOA-Si-OH was greater than 102°, which increased by 28°. The water absorption test showed that the modified polyurethane membrane nearly doubled its ability to prevent water penetration (from 18.11 % to 9.38 %). Although the introduction of silicone improved the water resistance of waterborne polyurethane, the mechanical properties were reduced. The introduction of IBOA into the silicone side chain improved the mechanical properties of polyurethane. Comparing WPU-Si with WPU-2, the tensile strength improved by 85.56 % (from 3.47 MPa to 6.44 MPa). Thermogravimetric analysis and dynamic thermomechanical analysis indicated that silicone reduced T<sub>g</sub> and thermal stability, but participation of IBOA made up for this deficiency. Terpene biobased compounds have great potential and application prospects in the modification of polymer materials.</p>

Preparation and Surface Properties of Silicone-Modified Polyester-Based Polyurethane Coats

Synthesis of CO2-Derived, Siloxane-Functionalized Poly(ether Carbonate)s and Waterborne Polyurethanes

Synthesis and Characterization of Eugenol‐based Silicone Modified Waterborne Polyurethane with Excellent Properties

Synthesis of High-Toughness Waterborne Polyurethane Utilizing Self-Emulsifying CO2-based Polyols

Siloxane-modified Polyester:Synthesis and Features of Its Powder Coatings

Synthesis of hydroxy silane coupling agent and the silane-terminated polyurethane chain-extended by butanediol

Synthesis and Properties of Triethoxysilane-Terminated Anionic Polyurethane and Its Waterborne Dispersions

Preparation and Characterization of Silicone Oil Modified Polyurethane Damping Materials

The role of segmental mixing on the mechanical properties and oxidative stability of polydimethylsiloxane-based polyetherurethane

Synthesis and characterization of organosilicon-modified self-matting waterborne polyurethane with excellent wear resistance

Terpene derivative-containing silicone two-component waterborne polyurethane for coatings

Preparation and Research of Hydrophobic PDMS/Nano-SiO2 Modified SiO2 Coating

Polydimethylsiloxane containing waterborne hydrophobic polyurethane coatings with good adhesion to metals: Synthesis and characterization

Effects of Polyether and Polyester Polyols on the Hydrophobicity and Surface Properties of Polyurethane/Polysiloxane Elastomers

Preparation and properties study of waterborne polyurethane synthesized by mixing polyester diols and isocyanates

Silane-Modified Hyperbranched Polyurethane with High Strength, High Transparency, and Low Viscosity

Preparation and properties of waterborne siloxane-containing polyurethane for moisture permeable textile coating

Preparation and Properties of Hydrophobic Polyurethane Based on Silane Modification

Surface properties of PDMS segmented/branched modified polyurethane copolymer

Synthetic scheme to increase the abrasion resistance of waterborne polyurethane–urea by controlling micro‐phase separation

Heat-Resistant and Anti-Corrosion Urethane-Silicone-based Coatings