Abstract:Polydimethylsiloxane (PDMS) is usually used to obtain favorable performances of waterborne polyurethane (WPU) such as higher hardness, exceptional thermal stability and lower interfacial tension. However, there is always a problem that waterborne polyurethane (WPU) often performs weak tensile strength, lower tenacity and brittle property at room temperature when polydimethylsiloxane (PDMS) is embedded into the backbone of polyurethane. The study aims to address the problem by constructing dual crosslinking structure, namely introducing trimethylolpropane as an intramolecular crosslinking agent into prepolymers and then adding waterborne polycarbodiimide (SK-400) as a post-crosslinking agent in order to further enlarge the degree of crosslinking and mainly make up for the shortcoming that mechanical property decreases when polydimethylsiloxane (PDMS) was inserted into molecule chains. Initially a novel inner-crosslinking prepolymer (SiWPU) comprising polydimethylsiloxane need to be synthesized successfully by inserting trimethylolpropane into prepolymers. Then the sample SiWPU-3 was picked out as a matrix resin and dropwise added polycarbodiimide (SK-400) as a post-crosslinking agent into the matrix resin (C–SiWPU). As pH was gradually lowering following the evaporation of triethylamine in the emulsion (C–SiWPU), carboxyl groups (COOH) in prepolymers started to react with SK-400 (NCN) to form twofold crosslinking structure. When 0%, 2%, 4%, 6%, and 8 wt% of waterborne polycarbodiimide (SK-400) was incorporated into the solution, the tensile strengths are 47.8 MPa, 57.7 MPa, 65 MPa, 57.6 MPa and 54.5 MPa and the elongation at break 732%, 756%, 798%, 707% and 700%. The crosslinking density of SiWPU-3 without the addition of waterborne polycarbodiimide (SK-400) is 3.86 × 10−3 mol/cm3. As 6 wt% of waterborne polycarbodiimide (SK-400) was added into the emulsion of SiWPU-3, the crosslinking density of C–SiWPU-6 (6 wt% SK-400) is 6.19 × 10−3 mol/cm3. The films show excellent extensibility and exceptional tenacity. Hence, the emulsion is able to be applied in leather industry.

Synthesis of hydroxy silane coupling agent and the silane-terminated polyurethane chain-extended by butanediol

The Effect of Silane Coupling Agent Containing Methacryloxy Group on UV-Curable Acrylate-Modified Polyurethane/SiO2 Hybrid Coatings

Synthesis and Characterization of Eugenol‐based Silicone Modified Waterborne Polyurethane with Excellent Properties

Synthesis of CO2-Derived, Siloxane-Functionalized Poly(ether Carbonate)s and Waterborne Polyurethanes

Synthesis of High-Toughness Waterborne Polyurethane Utilizing Self-Emulsifying CO2-based Polyols

Effect of Prehydrolysis VTMS on the Structure–Property of Silane‐Terminated Polyurethane

Terpene derivative-containing silicone two-component waterborne polyurethane for coatings

Silane-Modified Hyperbranched Polyurethane with High Strength, High Transparency, and Low Viscosity

Preparation and Surface Properties of Silicone-Modified Polyester-Based Polyurethane Coats

Preparation and Properties of Siloxane End-Capped Polyurethane

Synthesis and Surface Properties of Dihydroxybutyl Terminated-Polydimethylsiloxane Modified Polyurethane

Synthesis and Properties of Triethoxysilane-Terminated Anionic Polyurethane and Its Waterborne Dispersions

The Synthesis and Properties of Silylated Polyurethane-Urea Based on HTPB Sealant

Silane-terminated polyurethane applied to a moisture-curable pressure-sensitive adhesive using triethoxysilane

The Synthesis of Low-Viscosity Organotin-Free Moisture-Curable Silane-Terminated Poly(Urethane-Urea)s

Alkoxysilane Functionalized Polyurethane/Polysiloxane Copolymers: Synthesis and the Effect of End-Capping Agent

Synthesis of waterborne polyurethane by inserting polydimethylsiloxane and constructing dual crosslinking for obtaining the superior performance of waterborne coatings

Synthesis And Surface Property Of Siloxane-Modified Aqueous Polyurethane

Influence of Stiffness of Isocyanate on the Properties of Silane Modified Polyurea

Preparation and properties of waterborne siloxane-containing polyurethane for moisture permeable textile coating

Preparation and Properties of Silane End-Capped Polyurea