Abstract:In this study we synthesized LiFePO4/carbon/reduced graphene oxide (LFP/C/rGO) composite cathode materials using a method involving sol–gel processing, spray-drying, and calcination. To improve the electrochemical performance of LFP/C, we tested graphene oxides (GOs) of various morphologies as conductive additives, including pristine GO, three-dimensional GO, and hydrothermal porous GO (HTGO). Among our samples, the cathode material prepared through spray-drying with the addition of 1 wt% of HTGO (denoted SP-LFP/C/1%rHTGO) displayed the best electrochemical performance; its discharge capacities at 0.1C, 1C, 5C, and 10C were 160.5, 151.8, 138.8, and 130.3 mA h g−1, respectively. From measurements of its long-term cycling performance, the discharge capacity in the first cycle and the capacity retention after 30 cycles at 0.1C were 160.2 mA h g−1 and 99.6%, respectively; at 10C, these values were 132.2 mA h g−1 and 91.8%, respectively. The electronic conductivity of SP-LFP/C/1%rHTGO (6.58 × 10−5 S cm−1) was higher than that of the pristine LFP/C (9.24 × 10−6 S cm−1). The Li+ ion diffusivities (DLi+) of the SP-LFP/C/1%HTGO cathode, measured using AC impedance (3.91 × 10−13 cm2 s−1) and cyclic voltammetry (6.66 × 10−10 cm2 s−1 for discharge), were superior to those of the LFP/C cathode (9.31 × 10−15 cm2 s−1 and 1.79 × 10−10 cm2 s−1 for discharge, respectively). Galvanostatic intermittent titration revealed that the value of DLi+ was located in a reasonable range from 1 × 10−10 to 1 × 10−17 cm2 s−1; its value dropped to its lowest point when the state of charge was close to 50%. Thus, the use of spray-drying and the addition of conductive HTGO (having a 3D wrinkled morphology and interconnected pore structure) can enhance the electronic conductivity and Li+ ion diffusivity of LFP/C cathode materials, thereby improving the electrochemical performance significantly.

Improvement in Electrochemical Performance of Calcined LiNi0.5Mn1.5O4/GO

Enhanced Electrochemical Performance of LiNi0.8Co0.15Al0.05O2 Cathode Material via Li2TiO3 Nanoparticles Coating

Enhance electrochemical performance of Li LauMn1.904 by graphene oxide coating for lithium ion battery

Synthesis of Hierarchical and Bridging Carbon-Coated LiMn0.9Fe0.1PO4 Nanostructure As Cathode Material with Improved Performance for Lithium Ion Battery

Preparation, Lithium Storage Performance and Thermal Stability of Nickel‐Rich Layered LiNi0.815Co0.15Al0.035O2/RGO Composites

Surface Modification of Nanocrystalline LiMn2O4 Using Graphene Oxide Flakes

LiMnO2@rGO Nanocomposites for High‐performance Lithium‐ion Battery Cathodes

Synthesis and Superior Cathode Performance of Sandwiched LiMn2O4@rGO Nanocomposites for Lithium-Ion Batteries

Synthesis and characterization of LiMn0.8Fe0.2PO4/rGO/C for lithium-ion batteries via in-situ coating of Mn0.8Fe0.2C2O4·2H2O precursor with graphene oxide

Research based on graphene oxide composite with LiFe0.97Ni0.03PO4

Graphene/Ta2O5 co‐coating to improve the electrochemical performance of cathode material LiNi0.5Co0.2Mn0.3O2 for lithium‐ion batteries

Synthesis and Properties of LiFePO4/LiNi0.8Co0.15Al0.05O2 Composite Cathode Material Modificated by Graphene for Lithium Ion Battery

Improving the electrochemical properties of lithium iron(II) phosphate through surface modification with manganese ion(II) and reduced graphene oxide

Effect of carbon coating on electrochemical performance of Li 1.048 Mn 0.381 Ni 0.286 Co 0.286 O 2 cathode material for lithium-ion batteries

A new modification strategy for improving the electrochemical performance of high-nickel cathode material: V2O5 particles anchored on rGO sheets as a dual coating layer

High-rate Performance of LiNi0.5Mn1.45Al0.05O4 Cathode Material for Lithium-Ion Batteries

The preparation and electrochemical study of LiNi0.6Co0.2Mn0.2O2 cathode material for lithium-ion battery

Surface-engineering of Layered LiNi 0.815 Co 0.15 Al 0.035 O 2 Cathode Material for High-Energy and Stable Li-ion Batteries

Large-scale preparation of cobalt niobate/reduced graphene oxide composite materials for high-performance lithium-ion battery anodes

Modifying the morphology and structure of graphene oxide provides high-performance LiFePO4/C/rGO composite cathode materials

In Situ Self-Nucleophilic Synthesis of Nano-Li4ti5o12/reduced Graphite Oxide Composite with Mesopore-Oriented Porous Structure for High-Rate Lithium Ion Batteries