Modifying the morphology and structure of graphene oxide provides high-performance LiFePO4/C/rGO composite cathode materials

Wen-Chen Chien,Ya-Ru Li,She-Huang Wu,Yi-Shiuan Wu,Zong-Han Wu,Ying-Jeng James Li,Chun-Chen Yang

DOI: https://doi.org/10.1016/j.apt.2020.10.002

IF: 4.969

2020-11-01

Advanced Powder Technology

Abstract:<p>In this study we synthesized LiFePO₄/carbon/reduced graphene oxide (LFP/C/rGO) composite cathode materials using a method involving sol–gel processing, spray-drying, and calcination. To improve the electrochemical performance of LFP/C, we tested graphene oxides (GOs) of various morphologies as conductive additives, including pristine GO, three-dimensional GO, and hydrothermal porous GO (HTGO). Among our samples, the cathode material prepared through spray-drying with the addition of 1 wt% of HTGO (denoted SP-LFP/C/1%rHTGO) displayed the best electrochemical performance; its discharge capacities at 0.1C, 1C, 5C, and 10C were 160.5, 151.8, 138.8, and 130.3 mA h g⁻¹, respectively. From measurements of its long-term cycling performance, the discharge capacity in the first cycle and the capacity retention after 30 cycles at 0.1C were 160.2 mA h g⁻¹ and 99.6%, respectively; at 10C, these values were 132.2 mA h g⁻¹ and 91.8%, respectively. The electronic conductivity of SP-LFP/C/1%rHTGO (6.58 × 10⁻⁵ S cm⁻¹) was higher than that of the pristine LFP/C (9.24 × 10⁻⁶ S cm⁻¹). The Li⁺ ion diffusivities (<em>D</em>_Li⁺) of the SP-LFP/C/1%HTGO cathode, measured using AC impedance (3.91 × 10⁻¹³ cm² s⁻¹) and cyclic voltammetry (6.66 × 10⁻¹⁰ cm² s⁻¹ for discharge), were superior to those of the LFP/C cathode (9.31 × 10⁻¹⁵ cm² s⁻¹ and 1.79 × 10⁻¹⁰ cm² s⁻¹ for discharge, respectively). Galvanostatic intermittent titration revealed that the value of <em>D</em>_Li⁺ was located in a reasonable range from 1 × 10⁻¹⁰ to 1 × 10⁻¹⁷ cm² s⁻¹; its value dropped to its lowest point when the state of charge was close to 50%. Thus, the use of spray-drying and the addition of conductive HTGO (having a 3D wrinkled morphology and interconnected pore structure) can enhance the electronic conductivity and Li⁺ ion diffusivity of LFP/C cathode materials, thereby improving the electrochemical performance significantly.</p>

engineering, chemical