Fiber Properties of Tobacco Stems, Powder and Rods

Xiaofeng LIU,Youming LI,Yi HOU,Donghai CHEN,Jingtian CHEN

DOI: https://doi.org/10.3969/j.issn.1002-0861.2014.06.002

2014-01-01

Abstract:In order to study the fiber properties of raw material for paper-making process reconstituted tobacco,the chemical component in tobacco stems, powder and rods were determined, their fiber microstructure and fiber quality were analyzed, and the change of their surface appearance after hot water extraction was observed.The results showed that the fiber property of tobacco powder was similar to that of tobacco rods, but differed from that of tobacco stems obviously: 1) The ash, hot water extracts, holocellulose content in tobacco powder and rods were around 10%, 59%, 27% in contrast to 12.3%, 53.72%, 27.04% in stem, respectively. The contents of pentosan and lignin in the three kinds of material were similar(about 7% and 9%, respectively). 2) Upon the completion of hot water extraction, the wax layer on cell surface disappeared, cell wall became thinner, and fiber profile became clearer. 3) The fiber length of the mentioned material was shorter, the fines content was higher. Comparing with tobacco powder and rods, the fiber quality of tobacco stems was higher with the weighted average length of 0.76 mm and the fines content of 20.6%. 4) The process of reconstituted tobacco making at different beating conditions should adapt to material's fiber properties to obtain quality pulp. In addition, the beating degree should be carefully controlled to avoid over-beating.