Purification effects of glass flux on A356 melt
Hongjun Ni,Baode Sun,Haiyan Jiang,Chen Chen,Wenjiang Ding,倪红军,孙宝德,蒋海燕,陈晨,丁文江
IF: 3.752
2002-01-01
Transactions of Nonferrous Metals Society of China
Abstract:In order to remove hydrogen and inclusions from A356 alloy melt, a low melting-point glass flux, JDN-II, was developed. The results indicated that JDN-II flux has distinct effect of purification and protection on A356 alloy melt. When the dosage of the flux was 3 %, the content of hydrogen in A356 melt was only 2.6 mL/kg at 857 degreesC and 0.7 mL/kg even at 750 degreesC. In the meantime, the mechanical properties of the alloy increase greatly with the covering of 3 % JDN- H flux. Compared with no flux, the tensile strength of A356 alloy increases by 9.42 % and the elongation increases by 22%. The purification mechanism of JDN- H glass flux was discussed too.