Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma
Zheng Wang,Jun Wang,Yue Yuan,Long Cheng,Shao-Yang Qin,Arkadi Kreter,Guang-Hong Lu
DOI: https://doi.org/10.1016/j.jnucmat.2019.05.010
IF: 3.555
2019-01-01
Journal of Nuclear Materials
Abstract:Tungsten and tungsten-tantalum alloy with tantalum concentration of 10 wt%, sintered by spark plasma sintering, were exposed to deuterium plasma at similar to 500 K with flux of 1 x 10(21)-1 x 10(22) D m(-2)s(-1), an ion energy of 40 eV and fluence of 1 x 10(25)-1 x 10(26) D m(-2). After exposure, a large number of blisters with an average size of 1-2 mu m form on the surface of tungsten, and the area density of blisters increases with increasing irradiation fluence. However, the dominant morphology on the surface of tungsten-tantalum alloy is characterized by the striped microstructure, and exhibits a strong grain-orientation dependence. TDS results show two major desorption peaks located at similar to 650 K and similar to 770 K for tungsten and tungsten-tantalum alloy, respectively. Furthermore, the deuterium retention in tungsten is 4-6 times more than that in the tungsten-tantalum alloy. It is suggested that tantalum alloying can be expected to suppress the surface blistering and reduce the deuterium retention in tungsten. (C) 2019 Elsevier B.V. All rights reserved.