Abstract:Hexagonal boron nitride (h-BN) nanoparticles have attracted increasing attention due to their unique structure and properties. However, it is difficult to synthesize h-BN nanoparticles with uniform spherical morphology due to their crystal characteristic. The morphology control by tuning their precursor synthesis is a promising and effective strategy to solve this problem. Especially, the treatment temperature of precursors plays an important role in the morphology and surface area of h-BN nanoparticles. Herein, h-BN nanoparticles with different morphologies were synthesized via regulating the treatment temperature of precursors. The result shows that treatment temperature will affect the microstructure and state of precursor and further influence the morphology of h-BN products. Benefiting from the unique structure, the h-BN obtained using 250 °C precursors shows higher specific surface area (61.1 m2 g-1) than that of 85 °C (36.5 m2 g-1) and 145 °C (27.9 m2 g-1). h-BN products obtained using 250 °C precursors show higher specific surface area than that of 85 °C and 145 °C. The optimal condition for obtaining high-quality spherical h-BN is the pretreatment temperature of 250 °C and sintering temperature of 1300 °C. Importantly, compared with commercial h-BN nanoparticles, the synthesized h-BN nanoparticles show more uniform structure and larger specific surface area, indicating that sintering activity will be greatly improved. Furthermore, the reaction pathway and formation mechanism of h-BN was revealed by DFT calculations. The result shows that the five stationary states and five transition states exist in the reaction pathway, and the energy barrier can be overcome at high temperatures to form a ring h-BN. In view of its simplicity and efficiency, this work is promising for designing and guiding the synthesis of h-BN nanoparticles with uniform morphology.

Catalyzed synthesis of rhombohedral boron nitride in sodium chloride molten salt

Facile synthesis of hexagonal boron nitride nanoplates via molten-salt-mediated magnesiothermic reduction

From Highly Purified Boron Nitride to Boron Nitride‐Based Heterostructures: an Inorganic Precursor‐Based Strategy

New Process for Synthesis of Sodium Borohydride

A Facile Route to Prepare Boron Nitride Hollow Particles at 450 °C

A General Route for the Convenient Synthesis of Crystalline Hexagonal Boron Nitride Micromesh at Mild Temperature

Molten Salt Synthesis of ZnNb{sub 2}o{sub 6} Powder

A Low-Temperature Coreduction Route to Boron Nitride Flakes and Hollow Spheres

Low-temperature synthesis and benzene-thermal growth of nanocrystalline boron nitride

Process analysis and mechanism investigation of low temperature synthesis of nanoscale calcium hexaboride powder.

Liquid-Phase Exfoliation of Hexagonal Boron Nitride into Boron Nitride Nanosheets in Common Organic Solvents with Hyperbranched Polyethylene as Stabilizer

The Rietveld Refinement of Thermal Synthesized Rhombohedra Boron Nitride Micro-Rod

Synthesis and Morphology Control of Nanocrystalline Boron Nitride

Preparation of Isotropic Submicron Spherical Boron Nitride Particles by Restricted Template Method

One-Step Solid State Reaction to Synthesis of Hexagonal BN Crystals with Rod-Like Morphology

Molten salt synthesis of orthorhombic CrB and Cr2AlB2 ceramics

Formation of nanocrystalline BN with a simple chemical route

Preparation of BN Nanoparticle with High Sintering Activity and Its Formation Mechanism

Effect of ammonium chloride on the morphology of hexagonal boron nitride prepared by magnesium thermal reduction

Molten Salt Synthesis, Formation Mechanism, and Oxidation Behavior of Nanocrystalline HfB 2 Powders

Molten Salt Synthesis, Characterization, and Formation Mechanism of Superfine (hfxzr1‐x)b2 Solid‐solution Powders