Two-Site Occupancy Induced a Broad-Band Emission in Phosphor K 2 YZr(PO 4 ) 3 :Eu 2+ for White-Light-Emitting Diode Applications
Dan Zhao,Shi-Rui Zhang,Yan-Ping Fan,Bao-Zhong Liu,Ya-Nan Li,Lin-Ying Shi,Shao-Jie Dai
DOI: https://doi.org/10.1021/acssuschemeng.0c07082
2020-12-18
Abstract:Developing broad-band-emitting phosphors is very important to light-emitting diode (LED) lighting and displays. We introduced Eu<sup>2+</sup> to solid solutions K<sub>2</sub>YZr<sub>1–<i>y</i></sub>Hf<sub><i>y</i></sub>(PO<sub>4</sub>)<sub>3</sub> with a langbeinite-type structure to prepare a series of new phosphors. In this structure, two K<sup>+</sup> sites could be occupied by Eu<sup>2+</sup> cations to provide two different kinds of coordination environments, leading to broad emitting bands in the range of 390–700 nm. The coordination circumstance of Eu<sup>2+</sup> was analyzed by Gaussian fitting and time-resolved emission spectra. Furthermore, the emitting intensity and thermal stability can be improved by modulating the crystalline field via substituting Zr<sup>4+</sup> by Hf<sup>4+</sup>. When the Zr<sup>4+</sup> was fully substituted by Hf<sup>4+</sup>, the external quantum efficiency increased by 53.75%, giving a bright cyan emission. Finally, an archetype white-LED lamp was made using cyan phosphor K<sub>2</sub>YHf(PO<sub>4</sub>)<sub>3</sub>:0.04Eu, red phosphor CaAlSiN<sub>3</sub>:Eu<sup>2+</sup>, and a 365 nm LED chip, which realized an applicable color rendering index (<i>R</i><sub>a</sub> = 81) and a correlated color temperature (CCT = 3792 K).The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c07082?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c07082</a>.SEM images of KYZ<sub>1–<i>y</i></sub>H<sub><i>y</i></sub>P:0.04Eu (<i>y</i> = 0.4) at different magnifications (Figure S1a and S1b); elemental mapping of (Figure S1c) K, (Figure S1d) Y, (Figure S1e) Hf, (Figure S1f) Zr, (Figure S1g) P, (Figure S1h) O, and (Figure S1i) Eu, respectively; excitation (λ<sub>em</sub> = 600 nm) and emission (λ<sub>ex</sub> = 250 nm) spectra at room temperature of KYZP:0.04Eu (Figure 2); Eu 3d XPS region analysis of KYZP:0.04Eu; quantum efficiency of phosphor KYZP:0.04Eu<sup>2+</sup> (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c07082/suppl_file/sc0c07082_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology