Two-Site Occupancy Induced a Broad-Band Emission in Phosphor K 2 YZr(PO 4 ) 3 :Eu 2+ for White-Light-Emitting Diode Applications

Dan Zhao,Shi-Rui Zhang,Yan-Ping Fan,Bao-Zhong Liu,Ya-Nan Li,Lin-Ying Shi,Shao-Jie Dai

DOI: https://doi.org/10.1021/acssuschemeng.0c07082

2020-12-18

Abstract:Developing broad-band-emitting phosphors is very important to light-emitting diode (LED) lighting and displays. We introduced Eu²⁺ to solid solutions K₂YZr_1–<i>y</i>Hf_<i>y</i>(PO₄)₃ with a langbeinite-type structure to prepare a series of new phosphors. In this structure, two K⁺ sites could be occupied by Eu²⁺ cations to provide two different kinds of coordination environments, leading to broad emitting bands in the range of 390–700 nm. The coordination circumstance of Eu²⁺ was analyzed by Gaussian fitting and time-resolved emission spectra. Furthermore, the emitting intensity and thermal stability can be improved by modulating the crystalline field via substituting Zr⁴⁺ by Hf⁴⁺. When the Zr⁴⁺ was fully substituted by Hf⁴⁺, the external quantum efficiency increased by 53.75%, giving a bright cyan emission. Finally, an archetype white-LED lamp was made using cyan phosphor K₂YHf(PO₄)₃:0.04Eu, red phosphor CaAlSiN₃:Eu²⁺, and a 365 nm LED chip, which realized an applicable color rendering index (<i>R</i>_a = 81) and a correlated color temperature (CCT = 3792 K).The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c07082?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c07082</a>.SEM images of KYZ_1–<i>y</i>H_<i>y</i>P:0.04Eu (<i>y</i> = 0.4) at different magnifications (Figure S1a and S1b); elemental mapping of (Figure S1c) K, (Figure S1d) Y, (Figure S1e) Hf, (Figure S1f) Zr, (Figure S1g) P, (Figure S1h) O, and (Figure S1i) Eu, respectively; excitation (λ_em = 600 nm) and emission (λ_ex = 250 nm) spectra at room temperature of KYZP:0.04Eu (Figure 2); Eu 3d XPS region analysis of KYZP:0.04Eu; quantum efficiency of phosphor KYZP:0.04Eu²⁺ (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c07082/suppl_file/sc0c07082_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology