Photoluminescence Control of UCr4C4-Type Phosphors with Superior Luminous Efficiency and High Color Purity Via Controlling Site Selection of Eu2+ Activators

Wei Wang,Mengxuan Tao,Yixin Liu,Yi Wei,Gongcheng Xing,Peipei Dang,Jun Lin,Guogang Li

DOI: https://doi.org/10.1021/acs.chemmater.9b04089

IF: 10.508

2019-01-01

Chemistry of Materials

Abstract:Controlling the site selection of activators via chemical substitution to optimize and design luminescence materials is an essential part of rare-earth-activated phosphors. Herein, we report the UCr4C4-type CsKNa2-yLiy(Li3SiO4)(4):Eu2+ and CsKNa2(Li3Si1-zGezO4)4:Eu2+ phosphors, in which there are three crystallographic sites (Cs, K, and Na), and the site engineering for Eu2+ activators is utilized to tune the luminescence properties. First, Li+ ions are introduced to control the migration of Eu2+ ions from K sites to Na sites, realizing the spectral tuning from cyan narrow band [lambda(em) = 485 nm, full width at half-maximum (fwhm) = 27 nm] to green narrow band (lambda(em) = 526 nm, fwhm = 58 nm). Moreover, the variation of local lattice caused by Li+ ions improves the internal quantum yields from 39 to 82% as well as reduces the thermal quenching (90% @ 150 degrees C of integrated intensity at 20 degrees C). Second, the Ge4+ ions are introduced to control the shrinkage of the Na polyhedron for Eu2+ doping, leading to disappearance of the shoulder band in the green region. Simultaneously, the spectral blue shift should be ascribed to a synergistic effect of the reduction of crystal field splitting and Stokes shift. Thus, the blue-emitting CsKNa2(Li3GeO4)(4):Eu2+ phosphor is obtained, which has only one symmetric blue emission at 458 nm with fwhm = 26 nm. By employing a 370 nm UV chip, the as-fabricated white light-emitting diodes using CsKNaLi(Li3SiO4)(4):Eu2+ phosphor presents a superior luminous efficacy of 94.16 lm W-1, a corresponding color temperature of 5045 K, and a high color rendering index (95.8), demonstrating that the site engineering strategy based on the manipulation of chemical composition and crystal structure could be applied to tune spectral distribution and develop novel potential phosphors for practical optical application.