PRE-TRANSITION AND PSEUDO-ELASTICITY IN NiTi (fe) ALLOY

Shen Hui-min,HU Meishen,Gui Jianmin,Yuan Fang,Yening Wang,Guo Jinfang,) Beijing
IF: 1.797
1988-01-01
ACTA METALLURGICA SINICA
Abstract:The pseudo-elasticity of NiTi(Fe) alloy has been studied at diffe- rent temperatures and the stressed in situ X-ray and electron diffraction analysis have been performed at room temperature. The following results were obtained: (1) Above incommensurate transition temperature T_i, the stress-strain curve appears as superelastic loop of small loop area, due to the stress induced incommensurate phase as confirmed by in situ electron microscope experiment. (2) When R_s≤TT_i, the stress-strain curve turns into ferroelastic type from superelastic type, and the yield stress decreases while residual strain increases because of the elastic softening near R_s. R phase is present in NiTi alloy at room temperature (R_s is about 40℃). In situ X-ray diffraction has shown that stress induced reorientation of R domains takes place at the early stage of deviation from linearity on stress-strain curve. Further increasing the stress results in a yielding terrace of stress-strain curve associated with the appearance of diffraction patterns of stress induced martensite.
What problem does this paper attempt to address?