Surface topography evolution of TiO2/SnO2 coatings during thermal oxidation of Ti/Sn composite coatings

Liang Hao,Sujun Guan,Yun Lu,Wenzhi Qiu,Yiqiang He,Jizi Liu

DOI: https://doi.org/10.1016/j.surfcoat.2016.02.059

IF: 4.865

2016-01-01

Surface and Coatings Technology

Abstract:Mechanical coating followed by thermal oxidation in the atmosphere was used to prepare TiO2/SnO2 composite coatings. The coatings were characterized by X-ray diffraction (XRD), scanning electronic spectroscopy (SEM), energy dispersive spectrometer (EDS), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM) and so on. Results show that continuous rutile TiO2 coatings decorated with discrete SnO2 particles were formed during thermal oxidation at the temperature range of 873–1073K. Through the temperature range, a small quantity of SnO was formed. However, tiny amount of Ti2O3 was formed only when oxidation temperature was 1073K. The surface topography evolution of rutile TiO2 crystals during the thermal oxidation and relevant mechanism was also examined. Equiaxed, rod, columnar and needle TiO2 crystals with nanoscale were formed at temperatures from 873–1073K. The topography evolution indicates that the diffusion of oxygen species into the formed rutile TiO2 layer was predominant at 873K. It favored the growth of equiaxed crystals in the tangent plane rather than radial direction of Al2O3 ball substrate at the early stage of the thermal oxidation. However, the diffusion of Ti cations became prevailing compared with oxygen species at 1073K. The reaction of Ti and oxygen species occurred at the external surface of the formed TiO2 layer where rutile TiO2 needles were formed. During thermal oxidation at 973K, both the Ti cations and oxygen species were involved in the diffusion process and clusters of paired/parallel rutile TiO2 nanorods were formed. The addition of metallic Sn remarkably affected the surface topography and the grain size of rutile TiO2 crystals through regulating the diffusion of Ti cations and changing the local oxygen concentration surrounding Ti coatings. A proper additive amount refined the grains of rutile TiO2.