Abstract:In order to understand the strengthening and the failure mechanism of accumulative roll bonding (ARB)-processed AZ63 Mg alloy, the interfacial bonding and fracture behavior of an ARB-processed AZ63 sheet were studied through electron microscopic analysis. The correlation between the mechanical properties, the microstructure, and the ARB processing parameters of an AZ63 sheet were presented. The experimental results have demonstrated that the average grain size of AZ63 Mg alloy processed by ARB was remarkably refined from 12.8 μm to 5.7 μm when the ARB processing temperature was set to 623 K, indicating the occurrence and development of dynamic recrystallization (DRX) nucleation. With the increase in ARB passes, the microstructure obviously became uniform. However, after five passes of the ARB process at 623 K, grains with different crystallographic orientations at the interface can be rearranged to generate the coherent eutectic plane, which inhibits the further refinement of grain size. During the ARB process of the AZ63 Mg alloy, the grain refinement was controlled by twin-induced recrystallization and dynamic recrystallization. Microcracks at the bonded interface of the ARB1 sample were eliminated during the following 3~5 rolling passes at 623 K. After three passes of the ARB process at 623 K, the strength and elongation of the AZ63 Mg alloy increased from 232 MPa and 18.5% to 282 MPa and 26.3%, respectively. The tensile fracture morphology of the sample processed by three passes of ARB exhibited numerous dimples, and the slip lines caused by the cooperative deformation of refined grains can produce a network-like dimple structure, indicating that excellent ductile fracture characteristics could be obtained.

Microstructure, Mechanical Properties, and Texture Evolution of Aluminum Alloy 7005 by Accumulative Roll Bonding

Evolution of texture and microstructure during accumulative roll bonding of aluminum AA5086 alloy

Microstructural Evolution and Mechanical Properties of Multi-layered Aluminum Alloy 6061 Processed by Accumulative Roll Bonding

A Two-Scale Texture Modelling of AA1050 Aluminum Alloy after Accumulative Roll-Bonding (ARB)

Enhancing of aluminum alloy 1050-H4 tensile strength by accumulative roll bonding process

Enhancement of strength and ductility in 6061Al alloy processed by cross accumulative roll bonding

Microstructure Evolution and Mechanical Properties of AZ31 Alloy with Accumulative Roll Bonding

Texture and Mechanical Anisotropy of Ultrafine-Grained Aluminum Alloy AA6016 Produced by Accumulative Roll Bonding

Revealing the evolution mechanisms of microstructure, texture and mechanical behavior in Zr702 alloy plates fabricated by accumulative roll bonding

Microstructure and Texture Evolutions of Aa1050 Aluminum Alloy Cold Rolled to High Strains

Microstructural Evolution and Mechanical Properties of Pure Aluminum upon Multi-Pass Caliber Rolling

Microstructure of Commercial-Purity Aluminum Sheets Processed by Accumulative Roll Bonding (ARB) at a Series of Cyclic Preheating Conditions

Mechanical, microstructural, and textural evaluation of aluminum-MWCNT composites manufactured via accumulative roll bonding at ambient condition

Microstructural evolution and mechanical properties of multilayered ARB6/3/6 2N Al processed by accumulative roll bonding

Anisotropic Behavior of Al1050 through Accumulative Roll Bonding

Evolution of Microstructure, Texture and Mechanical Properties for Multilayered Al Matrix Composites by Accumulative Roll Bonding

Interfacial Bonding and Fracture Behaviors of AZ63 Magnesium Alloy Sheet Processed by Accumulative Roll Bonding

Stoichiometry and Texture Evolution of Individual Layers during Accumulative Roll Bonding of Al-Mg Laminated Composites

Effects Of Rolling Process On Microstructure And Mechanical Property Of 7050 Aluminum Alloy

Microstructure and Mechanical Properties of Al-Mg-Si Similar Alloy Laminates Produced by Accumulative Roll Bonding

Abnormal texture evolution of accumulative roll bonded Al-Cu by adding alumina particles