Abstract:Multi-layer crystallization and uncontrollable defects were the main factors that limiting the quality of Cu 2 ZnSn(S,Se) 4 (CZTSSe) films. Here a hybrid crystallization strategy was proposed to simultaneously improve the morphology and defect properties of CZTSSe film. Firstly, we found the variation of the microstructures (constitution, chemical environment of the elements, etc.) in precursor films can greatly alter the grain-growths of CZTSSe films. Detailed characterizations revealed that the chemical environment of S in the precursor film may influence the S-to-Se substitution of the film during the selenization process. This can further affect the grain-growth mechanism and the properties of CZTSSe film. While the S-to-Se substitution of the film mainly occurred below 500°C, the NaSe x on the surface of the film could dominate the grain-growth (Na-mechanism). For this mechanism, the CZTSSe film exhibited bi-layer morphology and relatively high band-tail energy, but shallow-acceptor was detected in the film. The solar cells based on the CZTSSe films reached the efficiency of 10.6%. As a comparison, liquid phase could be generated when the S-to-Se substitution of the film shifted to higher temperature (>500°C). In this condition, the grain-growth would be dominated by the liquid phase (LP-mechanism). Such mechanism can eliminate the multi-layer crystallization and reduce the band-tail energy, but the surface properties of the CZTSSe film was deteriorated and the formation of shallow-acceptor in CZTSSe was inhibited. The fabricated solar cells achieved the efficiency of 10.3%. Based on the results above, a bi-layer precursor film contained sub-layers with different microstructures was proposed to regulate the crystallization of CZTSSe. The co-existence of different microstructures in the precursor film could induce a hybrid grain-growth mechanism for the CZTSSe film (e.g., the Na-mechanism worked on the surface while the LP-mechanism worked in the bottom simultaneously). Such grain-growth mechanism can yield CZTSSe film with uniform morphology and favorable defect properties. The CZTSSe solar cells based on the hybrid grain-growth mechanism achieved the best efficiency of 12.6%. The investigation in this paper would provide new solutions for the crystallization regulation on CZTSSe photovoltaic material.

Aging Precursor Solution in High Humidity Remarkably Promoted Grain Growth in Cu2ZnSnS4 Films

Uniform monolayer Cu2ZnSn(S,Se)4 film based on novel precursor solution

Low-cost Fabrication of Cu 2 ZnSnS 4 Thin Films for Solar Cell Absorber Layers

Large-Grain Spanning Monolayer Cu2 ZnSnSe4 Thin-Film Solar Cells Grown from Metal Precursor

Preparation And Characterization Of Cu2znsns4 Thin Films And Solar Cells Fabricated From Quaternary Cu-Zn-Sn-S Target

Preparation of High-Quality Cu2ZnSnS4 Thin Films for Solar Cells Via the Improvement of Sulfur Partial Pressure Using a Static Annealing Sulfurization Approach

Improvement of grain growth and composition distribution of Cu2ZnSn(S,Se)4 by using chloride-based precursor solution

Enhance the Performance of CZTSSe Solar Cells Through Inhibiting the Cu2+, Tu, and (─COOH) Association Reaction

Facile single-component precursor for Cu2ZnSnS4 with enhanced phase and composition controllability

Coordination Engineering of Cu-Zn-Sn-S Aqueous Precursor for Efficient Kesterite Solar Cells

Simultaneously improving the morphology and defect properties of CZTSSe film via hybrid grain-growth mechanism

All-Layer Sputtering-Free Cu2Zn1-xCdxSnS4 Solar Cell with Efficiency Exceeding 7.5%

Self-Assembled 3D-Hierarchical Structure Cu2znsns4 Photocathodes by Tuning Anion Ratios in Precursor Solution

All Solution-Processed Cu2znsns4 Solar Cell By Using High-Boiling-Point Solvent Treated Ball-Milling Process With Efficiency Exceeding 6%

Visual Color Change During Spin‐coating Guiding the Quality of Cu2ZnSn(S,Se)4 Films

Benign Solutions and Innovative Sequential Annealing Processes for High Performance Cu2ZnSn(Se,S)4 Photovoltaics

Growth Mechanism and Properties of Nanostructure Cu 2 ZnSnSe 4 Thin Films and Solar Cells

Significantly Improving the Crystal Growth of a Cu 2 ZnSn(S,Se) 4 Absorber Layer by Air-Annealing a Cu 2 ZnSnS 4 Precursor Thin Film

Impact of Sol–gel Precursor Treatment with Preheating Temperature on Properties of Cu2ZnSnS4 Thin Film and Its Photovoltaic Solar Cell

In situ solvothermal growth of Cu2ZnSnS4 thin film for counter electrode of dye-sensitized solar cells

Novel solution processing of high-efficiency Earth-abundant Cu2 ZnSn(S,Se)4 solar cells.