Abstract:Phosphogypsum is an industrial waste generated in the production of fertilizers causing environmental problems. Calcined phosphogypsum (CPG) is obtained by low-temperature calcination and dehydration of phosphogypsum. CPG is mainly used to produce building materials. However, mechanical strength properties and water resistance of CPG materials is extremely poor, which leads to its relatively low utilization rate in construction industry. To address this issue, various amount of Ordinary Portland cement (OPC), fly ash (FA), rice husk (RH) and modified admixtures (AD) were mixed with the CPG to obtain CPG-based composite cementitious materials, which enhanced the water resistance and mechanical strength of the corresponding hardened materials. The influence of different contents of cement on the setting time, hydration heat, hydration products, mechanical properties, water absorption, heavy metal leaching and deterioration coefficient of the composite cementitious material is investigated. The results showed that the optimal mixing ratio of CPG: OPC: FA: RH was 57: 20: 10: 13 considering the water resistance and mechanical strength properties of CPG-based composite cementitious materials. On these conditions, the compressive strength, the flexural strength, water absorption and deterioration coefficient of the specimens at 28 days are 6.1 MPa, 4.6 MPa, 29.4% and 0.66 respectively, which were in line with the national standard of phosphorus building gypsum wallboard. It was demonstrated that two skeleton types are present in the samples prepared using CPG-based composite cementitious materials, which had a synergistic support effect on the structure. The first skeleton was formed by gypsum dihydrate crystals (CaSO 4 ·2H 2 O) and provided strength to the specimens at an early stage, while the second skeleton was formed by ettringite (AFt) and C–S–H gels, which provided strength at a later stage. The skeletons make the hardened materials denser and more waterproof. Moreover, the composite materials exhibited a positive solidification effect on heavy metals present in CPG.

An investigation on the anti-water properties of phosphorus building gypsum (PBG)-based mortar

Mechanical properties and soluble phosphorus solidification mechanism of a novel high amount phosphogypsum-based mortar

A Novel Gypsum-Based Self-Leveling Mortar Produced by Phosphorus Building Gypsum

The effects of admixtures on the durability properties of phosphogypsum-based cementitious materials

Development and optimization of phosphogypsum-based geopolymer cement

Green and Sustainable Superhydrophobic Phosphogypsum Mortar Coating with Self-Cleaning Properties and Water Resistance

Investigation of mechanical, microscopic, and leaching properties of coal-based solid waste geopolymer mortar activated by soda residue and phosphogypsum

Improving the mechanical property and water resistance of β-hemihydrate phosphogypsum by incorporating ground blast-furnace slag and steel slag

Low-Energy Consumption Preparation of Fine Waterproof Cementitious Material with High-Volume Phosphogypsum

Effect of Synergistic Modification of Building Materials Based on α-Hemihydrate Phosphogypsum by Portland Cement/H-PDMS on Water Resistance

Effects of phosphogypsum on hydration properties and strength of calcium aluminate cement

Influence of cement on properties of calcined phosphogypsum based composite cementitious materials

Study on the Chloride–Sulfate Resistance of a Metakaolin-Based Geopolymer Mortar

Hydration process and fluoride solidification mechanism of multi-source solid waste-based phosphogypsum cemented paste backfill under CaO modification

Thermal and Mechanical Properties Enhancement of Cement Mortar using Phosphogypsum Waste: Experimental and Modeling Study

Utilization of untreated-phosphogypsum as filling and binding material in preparing grouting materials

The Influence Mechanism of Molar Ratio on the Performance of Phosphogypsum-Modified Geopolymer Material

Mechanical Properties, Permeability and Microstructure of Steam-Cured Fly Ash Mortar Mixed with Phosphogypsum

Study on physical and chemical characteristics of β-hemihydrate phosphogypsum

Influence of calcination and GGBS addition in preparing β-hemihydrate synthetic gypsum from phosphogypsum