Abstract:The formation of dissimilar weld joints, including Al/Ti joints, is an area of research supported by the need for weight reduction and corrosion resistance in automotive, aircraft, aeronautic, and other industries. Depending on the cooling rates and chemical composition, rapid solidification of Al/Ti alloys during laser welding can lead to the development of different metastable phases and the formation of brittle intermetallic compounds (IMCs). The effort to successfully join aluminum to titanium alloys is associated with demands to minimize the thickness of brittle IMC zones by selecting appropriate welding parameters or applying suitable filler materials. The paper is focused on the numerical simulation of the laser welding–brazing of 2.0 mm thick titanium Grade 2 and EN AW5083 aluminum alloy plates using 5087 aluminum filler wire. The developed simulation model was used to study the impact of laser welding–brazing parameters (laser power, welding speed, and laser beam offset) on the transient temperature fields and weld-pool characteristics. The results of numerical simulations were compared with temperatures measured during the laser welding–brazing of Al/Ti plates using a TruDisk 4002 disk laser, and macrostructural and microstructural analyses, and weld tensile strength measurements, were conducted. The ultimate tensile strength (UTS) of welded–brazed joints increases with an increase in the laser beam offset to the Al side and with an increase in welding speed. The highest UTS values at the level of 220 MPa and 245 MPa were measured for joints produced at a laser power of 1.8 kW along with a welding speed of 30 mm·s−1 and a laser beam offset of 300 μm and 460 μm, respectively. When increasing the laser power to 2 kW, the UTS decreased. The results exhibited that the tensile strength of Al/Ti welded–brazed joints was dependent, regardless of the welding parameters, on the amount of melted Ti Grade 2, which, during rapid solidification, determines the thickness and morphology of the IMC layer. A simple formula was proposed to predict the tensile strength of welded–brazed joints using the computed cross-sectional Ti weld metal area.

Numerical Modelling and Experimental Verification of Thermal Characteristics and Their Correlations with Mechanical Properties of Double-Sided Laser Welded T-joint

Numerical and experimental study on thermal-metallurgical-mechanical behavior of high-strength steel welded joint

Establishment and Application of Material Models for Numerical Simulation of Welding Process

Experimental and Numerical Assessment of Temperature Field and Analysis of Microstructure and Mechanical Properties of Low Power Laser Annealed Welded Joints

Tensile failure analysis of laser stake-welded T-joints: X-ray tomography based conformal finite element and fractal theoretical approaches

Numerical study of thermal fluid dynamics and solidification characteristics during continuous wave and pulsed wave laser welding

Numerical and experimental study of residual stress in multi-pass laser welded 5A06 alloy ultra-thick plate

Mechanical Characterization and Prediction of Aluminum Alloy Laser Welding Joints Including Roles of Geometries and Porosity

Experimental and Numerical Study on Local Mechanical Properties and Failure Analysis of Laser Welded Dp980 Steels

Tensile Behaviors and Mechanical Property Analyses of T-Welded Joint for Thin-Walled Parts in Consideration of Different TIG Welding Currents Using Multiple Damage Models and Fracture Criterions: Numerical Simulation and Experiment Validation

Experimental investigations on mechanical properties of AA6061-T6 aluminum alloy joined by laser welding using digital image correlation

Microstructural evolution and numerical simulation of laser-welded Ti2AlNb joints under different heat inputs

Numerical Simulation of Temperature Fields during Laser Welding–Brazing of Al/Ti Plates

A Study of the Performance of Dissimilar Pulsed-Laser-Welded JSC590R/JAC980YL Steel Joints of Differential Thickness

Numerical simulation of molten pool flow behavior and keyhole evolution behavior in dual-laser beam oscillating bilateral synchronous welding of T-joints

Modeling of Temperature Field and Pool Formation During Linear Laser Welding of DP1000 Steel

A Numerical Simulation Method Considering Solid Phase Transformation and the Experimental Verification of Ti6Al4V Titanium Alloy Sheet Welding Processes

Effect of heat input on interfacial microstructure, tensile and bending properties of dissimilar Al/steel lap joints by laser Welding-brazing

Effect of Porosity Morphology and Elements Characteristics on Mechanical Property in T-joints During Dual Laser-Beam Bilateral Synchronous Welding of 2060/2099 Al-Li Alloys

Experimental and numerical investigation on temperature field and joint tensile failure for CF/PPS-Al alloy interlocking induction welding

Microstructure, Thermal Behavior and Tensile Properties of Laser Welded Bottom-Locking Joint for TA15 Titanium Alloy