Effect of the Thickness of Zn（BTZ）; Layer on the Electroluminescent Spectra of White Organic Light-emitting Devices

zhu feijian,hua yulin,yin shougen,deng jiachun,wu kongwu,niu xia,wu xiaoming

2006-01-01

Abstract:By fabricating white organic light-emitting devices of ITO/TPD/Zn（BTZ）;/Al,we found out that the EL spectra of the devices depended on the thickness of Zn（BTZ）; layer.When the thickness of Zn（BTZ）; was controlled at 80 nm,the EL spectra had one peak at 470 nm.When the thickness was controlled at 50 nm,the EL spectra had one peak at 580 nm.If the thickness was between 50 nm and 80 nm,the EL spectra simultaneously appeared two peaks at 470 nm and 580 nm,and the relative electroluminescence intensity also depended on the thickness.The more the thickness of Zn（BTZ）; closed to 80 nm（50 nm）,the stronger 470 nm（580 nm） peak’s intensity.When the thickness was coordinated to 65 nm,we got the white devices with CIE coordinated at（0.33,0.33）.To study the PL spectra of the device,we fabricated a thin film of TPD/Zn（BTZ）;.The PL spectra didn’t depend on the thickness of Zn（BTZ）;,and it’s peak at 480 nm was in agreement with other reports.The paper analyzed the above phenomenon.