Abstract:Bis-2-(2-hydmxyphenyl) benzothiazolate) zinc (Zn(BTZ)2) is one of the best white electroluminescent materials used in organic light-emitting diodes (OLEDs). White light, which is composed of three discrete peaks in R/G/B regions, is very important and particularly useful for full-color display. However, most of white OLEDs, so far, are fabricated with multilayer structures, which results in the complication of fabrication process and decline of quantum efficiency. So these devices are not suitable for the purpose of large-scale industrial manufacture. In this paper, firstly, Zn(BTZ )2 had been synthesized from the complex reaction between zinc acetate dihydrate and 2-(2-hydmxyphenyl) benzothiazolate. Then we used Zn(BTZ)2 as main light-emitting material and fabricated two types of organic white-light-emitting devices. The configurations of the devices are as follows: ITO/PVK: TPD/Zn(BTZ)2/Al and ITO/PVK: TPD/Zn(BTZ)2: Rubrene/Al. The bright and steady light emitting had been obtained, and the brightness of the devices came to 3200cd/m^2 and 2900cd/m^2 lat a driving voltage of 16V), respectively. We also measured the CIE coordinates of the above devices, they were (x=0.242, y=0.359) and (x=0.324, y=0.343), respectively. The latter CIE coordinate is very close to the equi-energy point (x=0.33, y=0.33), and the corresponding quantum efficiency value is 0.47%. This value is higher than the former one, which is 0.32%. Details on the white-light-emitting characteristics of the devices were explained by the curves of current density-voltage, optical current-voltage and quantum efficiency-current density, they were measured using a quantum efficiency measure system including the Keithley 485 Picoammeter and 2400 SourceMeter. We also discussed the emitting mechanisms of the material and the devices at last.

White Organic Light-Emitting Devices Using Zn(BTZ)2 Doped with Rubrene As Emitting Layer

Synthesis of Zn(BTZ)2 and Fabrication of White Organic Light-emitting Devices

Efficient White Organic Light-Emitting Device Based on a Thin Layer of Hole-Transporting Host with Rubrene Dopant

Bright White Organic Light-Emitting Diodes Based on Anthracene Derivatives and Rubrene

Efficient White Electroluminescent Device with Stable Emission Spectrum

Fabrication and Spectra Characteristics of High Efficiency White Organic Light-Emitting Diodes with Single Emitting Layer

Color stable white organic light-emitting diode based on a novel triazine derivative

White Light Emission Induced by Confinement in Organic Multiheterostructures

High Colour Rendering Index White Organic Light-Emitting Devices with Three Emitting Layers

White Organic Light Emitting Device with Dyestuff DCJTB Blended in Polymer

White Organic Light-Emitting Diodes with fine chromaticity tuning via ultrathin layer position shifting

High performance blue and white fluorescent organic electroluminescent devices with conventional electron transport material as blue emitter

Bright White Organic Light-Emitting Diodes Based On Two Blue Emitters With Similar Molecular Structures

White Organic Light Emitting Devices with Hybrid Emissive Layers Combining Phosphorescence and Fluorescence

Efficient White Light-Emitting Organic/Polymeric Electroluminescent Device

Solution-Processed White Organic Light-Emitting Diode Based on A Single-Emitting Small Molecule

White organic light-emitting diodes based on benzothiazole derivative

Multilayer White Organic Light-Emitting Diodes with A Single Host Material

Toward Achieving Single-Molecule White Electroluminescence from Dual Emission of Fluorescence and Phosphorescence

Efficient Organic Blue Fluorescent Light-Emitting Devices with Improved Carriers' Balance on Emitter Molecules by Constructing Supplementary Light-Emitting Layer

White Organic Light-Emitting Devices With A Bipolar Transport Layer Between Blue Fluorescent And Orange Phosphorescent Emitting Layers