Abstract:Based on a yellow fluorescent dye of 5, 6, 11, 12-tetraphenylnaphthacene (Rubrene), WOLEDs were fabricated, with doping structure and ultrathin layer structure utilized in the devices. By doping Rubrene into blue-emitting N,N'-bis-(1- naphthyl)-N,N'-biphenyl-1,1'-biphenyl-4,4'-diamine (NPB), the device with a structure of indium-tin-oxide (ITO)/NPB (40 nm)/NPB:Rubrene (0.25 wt%, 7 nm)/2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline (BCP) (30 nm)/Mg:Ag exhibited a warm white light with Commissions Internationale De L'Eclairage (CIE) coordinates of (0.38, 0.41) at 12 V. The electroluminescent spectrum of the OLED consisted of blue and yellow fluorescent emissions, the intensity of blue emission increased gradually relative to the orange emission with increasing voltage. This is mainly due to the recombination zone shifted towards the anode side as the transmission rate of electrons grows faster than that of holes under higher bias voltage. A maximum luminance of 7300 cd/m2 and a maximum power efficiency of 0.57 lm/W were achieved. Comparatively, by utilizing ultrathin dopant layer, the device with a structure of ITO/NPB (40 nm)/Rubrene (0.3 nm)/NPB (7 nm)/BCP (30 nm)/Mg:Ag achieved a low turn-on voltage of 3 V and a more stable white light. The peaks of EL spectra located at 430 and 560 nm corresponding to the CIE coordinates of (0.32, 0.32) under bias voltage ranging from 5 to 15 V. A maximum luminance of 5630 cd/m2 and a maximum power efficiency of 0.6 lm/W were achieved. The balanced spectra were attributed to the stable confining of charge carriers and exciton by the thin emitting layers. Hence, with simple device structure and fabricating process, the device with ultrathin layer achieved low turn-on voltage, stable white light emitting and higher power efficiency.

Efficient White Organic Light-Emitting Device Based on a Thin Layer of Hole-Transporting Host with Rubrene Dopant

High Efficiency All Phosphorescent White Light-Emitting Diodes Based on Conjugated Polymer Host

White Organic Light-Emitting Diodes Based on Doped and Ultrathin Rubrene Layer

Efficient bright white organic light-emitting diode based on non-doped ultrathin 5,6,11,12-tetraphenylnaphthacene layer

Fabrication of A New Organic Multilayer Phosphorescent White-Light-Emitting Device and Evaluation of Its Characteristics

Efficient White Electroluminescent Device with Stable Emission Spectrum

A White Organic Light Emitting Diode Based on Anthracene-Triphenylamine Derivatives

An Organic Light-Emitting Devices of Highly Efficient White Phosphor Using an Electron/exciton Blocker

Properties of White Organic Electroluminescent Device with Double Light-Emitting Layers Based Upon Different Hosts

Luminescent Properties of White Organic Light-Emitting Devices Based on Rubrene Ultrathin Layer

Influence of Dopant Concentration on Electroluminescent Performance of Organic White-Light-Emitting Device with Double-Emissive-Layered Structure

High-efficiency White Phosphorescent Organic Light-Emitting Diodes

White Organic Light-Emitting Devices Based on Fac Tris(2-Phenylpyridine) Iridium Sensitized 5,6,11,12-Tetraphenylnaphthacene

High-efficiency white organic light-emitting diodes based on phosphorescent iridium complex and 4,4′-Bis[N-1-napthyl-N-phenyl-amino]biphenyl emitters

Efficient White Organic Light-Emitting Devices Using 2,5-Diphenyl-1, 4-Distyrylbenzene with Two Trans-Double Bonds As Blue Emitter

A Novel White Organic Electroluminescent Device with Both Phosphorescent and Fluorescent Dopants

Highly Efficient Pure White Polymer Light-Emitting Devices Based on Poly(n-Vinylcarbazole) Doped with Blue and Red Phosphorescent Dyes

White Organic Light-Emitting Diodes with fine chromaticity tuning via ultrathin layer position shifting

Highly efficient white phosphorescent organic light-emitting devices using an electron/exciton blocker

Adjusting White Oleds With Yellow Light Emission Phosphor Dye And Ultrathin Npb Layer Structure

White Organic Light-Emitting Device with Both Phosphorescent and Fluorescent Emissive Layers