Abstract:The substrate of as-cast Ni-28 wt% Sn hypoeutectic alloy immersed in liquid nitrogen is rapidly remolten and solidified by laser surface remelting with a scanning velocity of 10 mm/s and the laser power of 1950 W. The microstructure of the substrate and its effect on the microstructure of the molten pool are investigated by scanning electron microscope carefully. It is found that the substrate of the Ni-28 wt%Sn ingot is composed of coarse primary α-Ni dendrites and the interdendritic (α-Ni+Ni3Sn) eutectic. The growth orientations of α-Ni dendrites and the interdendritic eutectic are distributed nearly randomly in the as-cast substrate. There are three kinds of microstructure characterstic zones from the top to the bottom of melted pool. The growth directions of α-Ni dendrites with the primary dendritic spacings ranging from 4.19 to 6.91 μm are approximately parallel to the laser scanning direction at the top of the molten pool due to the fact that the temperature gradient at the interface between the molten pool and substrate tends to be parallel to the laser scanning direction. In the middle of the molten pool, the epitaxial α-Ni columnar dendrites are found to be inclined to grow in the direction vertical to the bottom of the molten pool due to the fact that the temperature gradients in most zones of the molten pool are perpendicular to the bottom of the molten pool. The formation of new primary dendrites by the growth of the tertiary arm results in the decrease of primary dendritic spacing in comparison with that at the bottom of the molten pool. There are a small quantity of residual α-Ni primary phase and a large amount of (α-Ni+Ni3Sn) eutectic at the bottom of the molten pool. The microstructure of laser remolten zone is greatly influenced by the substrate microstructure, and the growth direction of the α-Ni dendrite in the molten pool is also affected remarkably by both the heat flux and the preferred crystal orientations for dendritic growth. Compared with the mixed lamella, rod and divorced (α-Ni+Ni3Sn) eutectic microstructures in the substrate, the eutectic structure in the molten pool is completely composed of the refined lamellar eutectic, which grows epitaxially in the direction perpendicular to the interface between the molten pool and the substrate at the bottom of molten pool. The eutectic lamellar spacing increases from the top (0.23 μm± 0.01 μm) to the bottom (0.42 μm± 0.02 μm) of the molten pool due to the interface growth velocity decreasing from the top to the bottom. The Kurz-Giovanola-Trivedi model for rapid dendritic growth and the Trivedi-Magnin-Kurz model for eutectic growth are used to estimate the growth undercooling of the microstructure in the molten pool respectively. It is found that the growth undercooling of dendrites and the eutectic in the molten pool should be between 50.4 K and 112.5 K, which is much larger than the critical undercooling for anomalous eutectic growth found in the high undercooled solidification in the previous researches. This phenomenon means that the critical undercooling for anomalous eutectic growth reported in the previous literature may be not the sufficient condition for generating the anomalous eutectic.

Three-dimensional reconstruction of anomalous eutectic in laser remelted Ni-30 wt.% Sn alloy.

Regular Eutectic and Anomalous Eutectic Growth Behavior in Laser Remelting of Ni-30wt%Sn Alloys

Numerical Simulation of Anomalous Eutectic Growth of Ni-Sn Alloy under Laser Remelting of Powder Bed

Microstructure Evolution in Laser Surface Remelting of Ni–33wt.%Sn Alloy

Primary Phase Growth Within Highly Undercooled Cu-Ge Eutectic Alloys

In Situ Observation of Remelting Induced Anomalous Eutectic Structure Formation in an Undercooled Ni-18.7 At.% Sn Eutectic Alloy

The Formation Mechanism of Anomalous Eutectic in Highly Undercooled Ni-Sn Eutectic Alloy

Mechanism of Anomalous Eutectic Formation in the Solidification of Undercooled Ni–Sn Eutectic Alloy

Formation of Anomalous Eutectic in Ni-Sn Alloy by Laser Cladding

In Situ and Ex Situ Studies of Anomalous Eutectic Formation in Undercooled Ni–Sn Alloys

Microstructural Evolution of Laser Surface Remelting Ni-28 Wt% Sn Alloy under Liquid Nitrogen Cooling

Non-equilibrium solidification of bulk undercooled Ni–P eutectic alloys

Anomalous Eutectic Formation in Undercooled Ni−P Eutectic Alloy

Remelting-induced Anomalous Eutectic Formation During Solidification of Deeply Undercooled Eutectic Alloy Melts

Microstructural Characteristics of Ni-Sb Eutectic Alloys under Substantial Undercooling and Containerless Solidification Conditions

Phase Selection and Re-Melting-induced Anomalous Eutectics in Undercooled Ni–38 Wt% Si Alloys

Rapid Solidification Kinetics and Mechanical Property Characteristics of Ni–Zr Eutectic Alloys Processed under Electromagnetic Levitation State

Microstructure Evolution of Ni-33％Sn Hypereutectic Alloy in Laser Rapid Solidification

Microstructural Characterization and Phase Separation Sequences During Solidification of Ni3Al-Based Superalloy

Phase Separation and Structure Evolution of Ternary Al–Cu–Sn Immiscible Alloy under Ultrasonic Levitation Condition

Microstructure Evolution of Ni-Sn Eutectic Alloy in Laser Cladding