Numerical Simulation of Anomalous Eutectic Growth of Ni-Sn Alloy under Laser Remelting of Powder Bed
Wei Lei,Cao Yongqing,Yang Haiou,Lin Xin,Wang Meng,Huang Weidong
DOI: https://doi.org/10.11900/0412.1961.2018.00139
IF: 1.797
2018-01-01
ACTA METALLURGICA SINICA
Abstract:Eutectic is one of the most commonly observed solidification patterns, the growth mor-phology of which is important to materials properties. Anomalous eutectic is typically coarser and globular than lamellar eutectic, which is commonly observed during solidification of binary eutectic alloy, including deep undercooled melt and laser remelting process. The morphological evolution mechanism of anomalous growth is still unknown due to the lack of simulation evidence. During laser remelting process, the anomalous eutectic is sandwiched between lamellar eutectic at the bottom of melt pool. Comparing to deep undercooled melt, laser remelting has simpler temperature field distribution, which can be simplified into directional solidification. Thus, simulations of anomalous eutectic growth in laser remelting process are feasible. In the present work, the anomalous eutectic growth mechanism under laser remelting conditions was simulated using a low mesh induced anisotropy cellular automaton (CA) model. Firstly, a two-dimensional lamellar eutectic CA model of CBr4-C2Cl6 alloy was established, and the morphological transition from 1 lambda O to 2 lambda O was simulated. The calculated results are in good agreement with experiments and phase field simulations. By setting the interface cells containing three phases (alpha, beta and liquid phases), the model can continuously change the alpha and beta phase volume fractions in the CA model, making it easier for the model to capture the instability of lamellar eutectic. Compared with the results of the phase field model, the intermediate 1 lambda O-2 lambda O state of oscillation instability of 1 lambda O and 2 lambda O which is consistent with the experimental results was calculated. Based on the above-mentioned binary eutectic CA model, the lamellar eutectic to anomalous eutectic transition at the bottom of the molten pool was simulated. Under the condition of initial low cooling rate, the fine lamellar eutectic is decoupled, it leads to the overgrowth of beta-Ni3Sn phase. During the subsequent accelerated cooling process, alpha-Ni nucleated in the liquid phase at the front of the solid/liquid interface, and the beta-Ni3Sn phase wrapped around the alpha-Ni phase forming anomalous eutectic morphology. During the laser remelting process, there is indeed a rapid change of solidification rate from zero to scanning speed rate from the bottom to the top of the melt pool, and therefore coincides with the solidification conditions of the variable pulling velocity used in the CA simulations.