Abstract:Anomalous eutectics are argued to form due to the remelting of the primary solid during solidification of deeply undercooled eutectic alloy melts. As an indicator of the tendency for anomalous eutectic formation, the remelted fraction of the primary eutectic was analyzed systematically based on the eutectic dendrite growth theory. For eutectic alloys with either larger equilibrium solute distribution coefficients or gentle liquidus slopes, the primary eutectic is highly supersaturated with solute and more prone to remelting. When the eutectic composition is set to different values, (e.g. the eutectic point is closer to one phase of the eutectic), the two eutectic phases under rapid growth change their compositions simultaneously, but their remelted fractions during temperature recalescence do not vary significantly. Three representative binary eutectic alloys Ag–39.9at.%Cu, Ni–19.6at.%P and Pd–16.0at.%P – their eutectic products are solid solution–solid solution, solid solution–stoichiometric intermetallic compound and stoichiometric intermetallic compound–stoichiometric intermetallic compound, respectively, were solidified at large undercooling. Anomalous eutectics were observed in the first two eutectic alloys whose eutectic structure consists of at least one solid solution phase, whereby the stoichiometric intermetallic compound phase remained highly oriented whereas the solid solution phase had a near random distribution of orientations. For the Pd–16.0at.%P alloy, however, the primary eutectic retained its original morphology as the final solidification structure regardless of the degree of undercooling. All these experimental results validate the argument that anomalous eutectics result from the remelting of the primary solid.

Remelting-induced Anomalous Eutectic Formation During Solidification of Deeply Undercooled Eutectic Alloy Melts

Non-equilibrium solidification of bulk undercooled Ni–P eutectic alloys

Anomalous Eutectic Formation in Undercooled Ni−P Eutectic Alloy

Microstructural Characteristics of Ni-Sb Eutectic Alloys under Substantial Undercooling and Containerless Solidification Conditions

Investigation of the Origin of Anomalous Eutectic Formation by Remelting Thin-Gauge Samples of an Ag-Cu Eutectic Alloy

Formation Mechanism of Anomalous Eutectics in Highly Undercooled Ag-39.9 At%Cu Alloys

Primary Phase Growth Within Highly Undercooled Cu-Ge Eutectic Alloys

Remelting of Primary Solid in Rapid Solidification of Deeply Undercooled Alloy Melts

The Formation Mechanism of Anomalous Eutectic in Highly Undercooled Ni-Sn Eutectic Alloy

Ternary eutectic and peritectic solidification of undercooled liquid Fe–Mo–Si alloys

Formation Mechanism of the Primary Faceted Phase and Complex Eutectic Structure Within an Undercooled Ag–Cu–Ge Alloy

Formation Mechanism of Primary Phases and Eutectic Structures Within Undercooled Pb-Sb-Sn Ternary Alloys

Rapid Growth of Ternary Eutectic Un Der High Undercooling Conditions

Anomalous Eutectic Formation in the Solidification of Undercooled Co–Sn Alloys

Phase Selection and Re-Melting-induced Anomalous Eutectics in Undercooled Ni–38 Wt% Si Alloys

Ternary Eutectic Growth in A Highly Undercooled Liquid Alloy

Mechanism of Anomalous Eutectic Formation in the Solidification of Undercooled Ni–Sn Eutectic Alloy

A Triple Comparative Study of Primary Dendrite Growth and Peritectic Solidification Mechanism for Undercooled Liquid Fe59ti41 Alloy

Three-dimensional reconstruction of anomalous eutectic in laser remelted Ni-30 wt.% Sn alloy.

Metastable Phase Separation And Rapid Solidification Of Undercooled Co40fe40cu20 Alloy

Solute Redistribution Profiles During Rapid Solidification of Undercooled Ternary Co-Cu-Pb Alloy