Novel Partial Remelting Process and Microstructure Evolution of Semi-Solid 2024 Alloy

Wang Shuncheng,Li Yuanyuan,Chen Weiping,Zheng Xiaoping

DOI: https://doi.org/10.3321/j.issn:1002-185X.2009.z1.043

2009-01-01

Rare Metal Materials and Engineering

Abstract:A two-step partial remelting process was proposed and applied to perform partial remelting experiments on the semi-solid 2024 alloy billet prepared by low superheat pouring. In this process, the semi-solid billet was firstly heated isothermally over liquids temperature for a few seconds, and then held isothermally at solidus-liquidus zone temperature. The microstructure evolution of the semi-solid billet, during the two-step partial remelting process was studied and compared with that during isothermal partial remelting process. The results show that the formation rate of liquid phase of the semi-solid billet during the two-step partial remelting process is faster than that during the isothermal partial remelting process. The accelerating of liquid phase formation during the two-step partial remelting process can restrain the coalescence of grains to a certain extent, and thus reduce the growth rate of grains and promote the spheroidization rate. The grains of the semi-solid billet partially remelted by the two-step partial remelting process are finer and rounder than those by the isothermal partial remelting process.