Abstract:Because of its excellent biocompatibility and low allergenicity, titanium has been widely used for bone replacement and tissue engineering. To produce a desirable composite with enhanced bone response and mechanical strength, in this study bioactive calcium phosphate (CaP) and gelatin composites were coated onto titanium (Ti) via a novel urease technique. The cellular responses to the CaP/gelatin/Ti (CaP/gel/Ti) and bone bonding ability were evaluated with proliferation and osteogenic differentiation of mesenchymal stem cells (MSCs) on CaP/gel/Ti and CaP/Ti in vitro. The results showed that the optical density values, alkaline phosphatase expression and genes expression of MSCs on CaP/gel/Ti were similar to those on CaP/Ti, yet significantly higher than those on pure Ti (p < 0.05). CaP/gel/Ti and CaP/Ti rods (2 mm in diameter, 10 mm in length) were also implanted into femoral shaft of rabbits and pure Ti rods served as control (n = 10). Histological examination, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) measurements were performed at 4 and 8 weeks after the operation. The histological and SEM observations demonstrated clearly that more new bone formed on the surface of CaP/gel/Ti than in the other two groups at each time point. The CaP/gel/Ti bonded to the surrounding bone directly with no intervening soft tissue layer. An interfacial layer, containing Ti, Ca and P, was found to form at the interface between bone and the implant on all three groups by EDS analysis. However, the content of Ca, P in the surface of CaP/gel/Ti implants was more than in the other two groups at each time point. The CaP/gel/Ti modified by the urease method was not only beneficial for MSCs proliferation and osteogenic differentiation, but also favorable for bone bonding ability on Ti implants in vivo, suggesting that Ti functionalized with CaP and gelatin might have a great potential in clinical joint replacement or dental implants.

In Vitro Study on the Osteogenesis Enhancement Effect of BMP-2 Incorporated Biomimetic Apatite Coating on Titanium Surfaces

Effects of Nacre-Coated Titanium Surfaces on Cell Proliferation and Osteocalcin Expression in Mg-63 Osteoblast-Like Cells

Biomimetic ECM coatings for controlled release of rhBMP-2: construction and biological evaluation

Influence of Multilayer Rhbmp-2 DNA Coating on the Proliferation and Differentiation of MC3T3-E1 Cells Seeded on Roughed Titanium Surface.

Cell Biocompatibility of Hydroxyapatite/Silk Fibroin Composite Scaffolds Carrying Bone Morphogenetic Protein

Bone Response to the Multilayer BMP-2 Gene Coated Porous Titanium Implant Surface.

In vivo and in vitro biological efficacy of double-layer coating of titanium with gelatin and calcium phosphate

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

BMP2-encapsulated chitosan coatings on functionalized Ti surfaces and their performance in vitro and in vivo

Bone Responses to Rough Titanium Implants Coated with Biomimetic Ca-P in Rabbit Tibia.

Promotion of Osteogenic Differentiation of Stem Cells and Increase of Bone-Bonding Ability in Vivo Using Urease-Treated Titanium Coated with Calcium Phosphate and Gelatin

Fabrication and in vitro evaluation of the collagen/hyaluronic acid PEM coating crosslinked with functionalized RGD peptide on titanium.

Apatite Layer-Coated Titanium for Use As Bone Bonding Implants

PTH coatings on titanium surfaces improved osteogenic integration by increasing expression levels of BMP-2/Runx2/Osterix

In Vivo Comparison of Bone Formation on Titanium Implant Surfaces Coated with Biomimetically Deposited Calcium Phosphate or Electrochemically Deposited Hydroxyapatite

Polyelectrolyte Multilayer Coating with Two Regulatory Molecules on Titanium: Construction and Its Biological Effects

Osteoblast Response to Porous Titanium Surfaces Coated with Zinc-Substituted Hydroxyapatite

Enhanced Loading and Controlled Release of Rhbmp-2 in Thin Mineralized Collagen Coatings with the Aid of Chitosan Nanospheres and Its Biological Evaluations.

Biomimetic titanium implant coated with extracellular matrix enhances and accelerates osteogenesis.

Sustained delivery of BMP-2 enhanced osteoblastic differentiation of BMSCs based on surface hydroxyapatite nanostructure in chitosan-HAp scaffold

Biomimetic Calcium Phosphate Coatings for Bioactivation of Titanium Implant Surfaces: Methodological Approach and In Vitro Evaluation of Biocompatibility