Abstract:(Al,Si)3(Zr,Ti)-D022/D023 are phases that may form in aerospace and automotive aluminium alloys. The substitution of Zr/Ti in these solid solutions is widely reported in the literature; however, it remains relatively unexplored for Si. In this work, in situ precipitation of (Al,Si)3(Zr,Ti)-D022/D023 intermetallics was performed using Al-Si-Zr-Ti alloys. The precipitation, sedimentation and concentration of numerous intermetallic particles were accomplished by filtrating the residual molten aluminium using a temperature/pressure-controlled vessel adapted with a PoDFA filter. A combination of SEM, TEM, XRD and EMP analysis allowed the identification of (Al,Si)3(Zr,Ti)-D022/D023 intermetallics concentrated within α -FCC matrices of non-Si-doped (sample S2) and Si-doped (samples S4 and S6) alloys. EDS analysis confirmed that Zr and Ti substitute each other in the D022 and D023 phases, whereas Si substitutes in Al sites. Acceptance of Si inside the D023 phase was not expected according to FTlite (FactSage) and TCAL7 (Thermo-Calc) databases. Additionally, Si was found to enhance the formation of (Al,Si)3(Zr,Ti)-D022 intermetallics with high Zr-content, contrary to FactSage 7.3 predictions. TEM results showed intermetallic/FCC crystal coherency for samples S2 and S6, implying that these intermetallics acted as nucleation sites for the Al-phase due to their small lattice mismatch. Furthermore, Si site occupancy was calculated for both (Al,Si)3Ti-D022 and (Al,Si)3Zr-D023 phases via DFT, showing that sites 2b and 4e are the most favorable for Si occupation, respectively. Finally, a thermodynamic model is derived to describe Si substitution upon solidification. Experimental and numerical examinations indicate that Si substitution preferentially occurs in the D022 intermetallics compared to the D023 phase.

The Isothermal Section of the Fe-Si-Ti-93 at.% Zn Quaternary System at 450 °C

Experimental study of the phase relations in the Fe–Cr–Si ternary system at 700°C

Isothermal Section of Ternary Sn-Zn-Ni Phase Equilibria at 250 °C

Isothermal Section Of Mn-Zr-Si Ternary System At 600 Degrees C

Phase Equilibria in the Ni-Sn-Zn System at 500°C

Experimental Investigation of Phase Equilibria in the Co-Ta-Si Ternary System

The melting diagram of the Ti-corner of the Ti–Zr–Si system and mechanical properties of as-cast compositions

Experimental Study on Phase Relationships in the Co-rich Portion of the Co–Ti–Zr System

Experimental Investigation and Thermodynamic Assessment of the Mo–Ni–Zr Ternary System

Isothermal section of the ternary Sn-Cu-Ni system and interfacial reactions in the Sn-Cu/Ni couples at 800 °C

Liquidus Projection and Isothermal Section of the Ag-In-Zn Ternary System

Phase Equilibria of the Sn–Zn–Cu Ternary System

Phase equilibria in Ni–Ti–Ta ternary system

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Experimental determination of phase diagram in the Zn-Fe binary system

Phase equilibria in the Fe–Nb–Zr ternary system at 1,200 °C

Thermodynamic Evaluation of the Fe-Zn Binary System with Reference to the Latest Experimental Phase Diagram

Phase Equilibria in the Ti-Rich Portion of the Ti-Ga-Sn System

Synthesis and characterization of (Al,Si)3(Zr,Ti)-D022/D023 intermetallics: Understanding the stability of silicon substitution

Phase diagrams of the Ag-In-Zn ternary system

Experimental isothermal section of the system Cr-Nb-Ru at 1100 °C