Abstract:Despite zirconia (ZrO2) ceramics and lithium disilicate (Li2Si2O5) glass-ceramics have been widely applied on the market for dental restorations, composites that can combine the advantages of both are still demanded. Here we introduced a ZrO2-Li2Si2O5 ceramic with minimized glass phases that fabricated through a sol-gel method and subsequent pressureless sintering. ZrO2-Li2Si2O5 powders were obtained after the gel precursors were heat treated under 800 °C. The gel-derived powders were molded and pressureless sintered under 900-1000 °C to investigate their sintering properties. From the microstructures of the sintered samples, we knew that the densification process was dominated by the growth of Li2Si2O5 grains instead of the growth of ZrO2 grains. Increasing in Li2Si2O5 content can promote ceramic densification. Interestingly, reactions between ZrO2 and Li2Si2O5 were observed with sintering temperature higher than 916 °C, which can increase the porosity of the ceramics. Therefore, both the content of Li2Si2O5 and sintering temperature should be well adjusted to achieve samples with desired properties. Finally, ceramics with flexural strength of 226 MPa and porosity of 0.4% were achieved from powders with moderate Li2Si2O5 content after sintering at 1000 °C.

Preparation and Dielectric Properties of SiO2/silicate-1 Ceramics

Synthesis and microwave dielectric properties of (Ca0.7Mg0.3)SiO3 nanopowder prepared at low temperature

Effect of A-site Substitution on Sintering and Dielectric Properties of ZnO-0.5SiO2 Ceramics

Low-Temperature Sintering and Microwave Dielectric Properties of (ca0.9mg0.1)sio3 Ceramic with Li2co3 Addition

Synthesis and Microwave Dielectric Properties of (Ca_(0.7)Mg_(0.3))SiO_3 Ceramic by Sol-Gel Process

Phase Characterization and Dielectric Properties of Zn2SiO4 Ceramics Derived from a Sol-Gel Process

Low-temperature Sintering and Microwave Dielectric Properties of (zn1−xcox)2sio4 Ceramics

Phase purifying and dielectric improvement in Zn2SiO4 ceramics via simply controlling the particle size of SiO2

Effects of Zn2+ Substitution on the Sintering Behaviour and Dielectric Properties of Li2Mg1−xZnxSiO4 Ceramics

Synthesis and Microwave Dielectric Properties of (Ca<SUB>0.7</SUB>Mg<SUB>0.3</SUB>)SiO<SUB>3</SUB>Ceramic by Sol-Gel Process: Synthesis and Microwave Dielectric Properties of (Ca<SUB>0.7</SUB>Mg<SUB>0.3</SUB>)SiO<SUB>3</SUB>Ceramic by Sol-Gel Process

Sintering characteristics and crystallization for sol–gel-derived powders for low-dielectric and low-temperature sintering ceramics

Sol-gel preparation of ZrO2–Li2Si2O5 ceramics and their sintering properties

Modulation of the Microwave Dielectric Properties of Si-Based Olivine Structured Ceramics Through the Variation of A-Site Ions

Microstructure and Microwave Dielectric Properties of (zn1−xmgx)2sio4 Ceramics

Microstructure and Microwave Dielectric Properties of Tio2-Doped Zn2sio4 Ceramics Synthesized Through the Sol-Gel Process

Microwave Dielectric Properties of (1−x)sio2−xtio2 Ceramics

Microstructure and Properties of ZrO 2 -, TiO 2 -Doped Ca–Si–B Based Ceramics

Mechanical and Dielectric Properties of Porous Si3n4-Sio2 Composite Ceramics

Synthesis and Microwave Dielectric Properties of CaO–MgO–SiO2 Submicron Powders Doped with Li2O–Bi2O3 by Sol–gel Method

Fabrication and properties of Si2N2O ceramics for microwave sintering furnace

Effect of SiO2/BaO ratio on sintering behavior, crystallization behavior, and properties of SrO–BaO–B2O3–SiO2 glass-ceramics