Abstract:In mechanical applications, defect-based fatigue cracking is a significant strength-limiting failure mode of additively manufactured composites that is not yet fully understood in the service environment. In this paper, axial loading tests were carried out at 25 °C and 450 °C, and then the effects of temperature on the long-life fatigue properties of the TiC-reinforced Ti6Al4V composite fabricated by Laser Powder Bed Fusion (LPBF) were investigated by combining the techniques of electron backscatter diffraction, X-ray computed tomography, and 3D morphological reconstruction. With the increase in temperature, the fatigue strength of the LPBF TiC/Ti6Al4V composite decreases significantly. The main causes of the interior failure at both temperatures are the inhomogeneous hardening zone (IHZ) formed by TiC agglomeration and the pore defect generated during the manufacturing process. The presence of brittle IHZ and pores causes stress concentration, which leads to crack nucleation. When a crack reaches the specimen surface, the combined effects of temperature and oxygen accelerate the ensuing crack propagation at high temperature. Based on the temperature effect, material properties, and the statistical distribution of defects, a model has been developed to predict the P-S-N curves at both temperatures. This model performed well in estimating the fatigue strength at 10 9 cycles. These findings provide new insights into the defect-related fatigue failure mechanisms and strength evaluation of the LPBF TiC/Ti6Al4V composite at different temperatures.

Effects of defects on fatigue behavior of TC17 titanium alloy for compressor blades: Crack initiation and modeling of fatigue strength

High cycle and very high cycle fatigue of TC17 titanium alloy: Stress ratio effect and fatigue strength modeling

Fatigue cracking behavior and life assessment of TC11 titanium alloy in very high cycle regime at two working temperatures

Defect-based fatigue crack nucleation and strength evaluation of additively manufactured TiC/Ti6Al4V titanium matrix composite at different temperatures

Effect of surface roughness on the fatigue failure and evaluation of TC17 titanium alloy

The Effect of Defect Characteristics on Prediction of Fatigue Life of TC4 Titanium Alloy Welded Joints

Microstructure based cracking behavior and life assessment of titanium alloy under very-high-cycle fatigue with elevated temperatures

Effect of Cutting Surface Integrity on Fatigue Properties of TC17 Titanium Alloy

Molecular dynamics simulation of effects of loading parameters on fatigue crack growth behavior in titanium single crystal

Effect of surface high-density twinned structure on the fatigue crack initiation of Ti-6Al-4V

The Fatigue Deformation Mechanism of TC17 Alloy with Residual Stress and Microstructure Dual Gradients

Crystal plasticity modeling fatigue behavior in bimodal Ti–6Al–4V: Effects of microdefect and lamellar orientation

High-temperature fatigue behavior of TC17 titanium alloy and influence of surface oxidation

Crack Initiation Mechanism and Life Prediction of Ti60 Titanium Alloy Considering Stress Ratios Effect in Very High Cycle Fatigue Regime

Fatigue life prediction for LPBF-fabricated Ti-6Al-4V up to very-high-cycle regime based on continuum damage mechanics incorporating effect of defects

Effect of stress ratio on VHCF behavior for a compressor blade titanium alloy

The mechanism of internal fatigue-crack initiation and early growth in a titanium alloy with lamellar and equiaxed microstructure

The effect of surface roughness and microstructure on fretting fatigue properties of TC21 based on hierarchical multiscale modeling

Effects of Surface Defects on Rolling Contact Fatigue in 10Cr4ni4mo4v

Effect of Stress Ratio on Very High Cycle Fatigue Properties of Ti-10V-2Fe-3Al Alloy with Duplex Microstructure

Fatigue Crack Initiation and Propagation Dominated by Crystallographic Factors in TiB/near α-Ti Composite