Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Mechanical and Electrical Properties of MoSi2-based Ceramics with Various ZrB2-20 Vol% SiC As Additives for Ultra High Temperature Heating Element

Preparation and Mechanical Properties of ZrB2-based Ceramics Using MoSi2 As Sintering Aids

Novel (Zr, Ti)(C, N)–SiC ceramics via reactive hot-pressing at low temperature

Microstructure and properties of silicon carbide whisker reinforced zirconium diboride ultra-high temperature ceramics

Influence of the Metal Particle Size and Sintering Process on the Electrical Resistivity of M-Zro2/30%mo Cermet

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

Mechanical Properties of Short Carbon Fiber Reinforced ZrB2–SiC Ceramic Matrix Composites

Effects of SiC contents on the microstructure and mechanical properties of Al4SiC4–SiC ceramic composites

Preparation, mechanical properties, and toughening mechanisms of SiCw/SiCp‐reinforced zirconia‐toughened alumina ceramics

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Thermal and Electrical Transport in ZrB2-SiC-WC Ceramics Up to 1800 °C

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Effect of SiC on the anti-ablation resistance and flexural strength of (Hf-Ta-Zr)C-C/C composites

Ablation behaviour of ultra-high temperature ceramic matrix composites: Role of MeSi2 addition

Microstructures and mechanical properties of high-entropy (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C ceramics with the addition of SiC secondary phase

Preparation and Characterization of ZrB 2 -Sic Ultra-High Temperature Ceramics by Microwave Sintering

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Effects of Short Carbon Fiber on Mechanical Properties of ZrB2-SiC Ultra-high Temperature Ceramics

Ultrahigh‐temperature tensile behaviors of ZrB2–SiC ceramics

Effects of MgSiN2 Addition and Post-Annealing on Mechanical and Thermal Properties of Si3N4 Ceramics

Microstructure, mechanical and high-temperature dielectric properties of zirconia-reinforced fused silica ceramics