Phase Transition Mechanism of Fe1.1se0.5te0.5 Fabricated by High-Energy Ball Milling Aided Sintering Method

Jixing Liu,Chengshan Li,Shengnan Zhang,Jianqing Feng,Pingxiang Zhang,Lian Zhou

DOI: https://doi.org/10.1109/tasc.2017.2744329

IF: 1.9489

2017-01-01

IEEE Transactions on Applied Superconductivity

Abstract:We report the phase transition mechanism of Fe1.1Se0.5Te0.5 fabricated by the high-energy ball milling (HEBM) aided sintering method, which was achieved by multi-step quenching heat treatment process. The precursor powders, composed of Fe and (Se, Te)(ss), were synthesized via an HEBM method for 2 h using Fe, Se, and Te mixture powders. Under the sintering temperature of 400 degrees C, the two compositions began to diffuse into each other and Fe(Se, Te)(2) phase with uniform Se and Te distribution was formed directly. With further increasing temperature to 500 degrees C, tetragonal beta-Fe(Se, Te) phase was obtained owing to the elemental diffusion of Fe into Fe(Se, Te)(2). Due to the effective shortened length of diffusion paths, the superconducting phase formation temperature was similar to 100 degrees C lower during our HEBM aided sintering method than that in the traditional solid state sintering method. Finally, a critical temperature of 14.2 K was observed in the final treatment sample, which was sintered for 12 h at 700 degrees C with a slow cooling rate followed by an annealing process under oxygen atmosphere for 24 h. This T-c value could demonstrate a good superconducting phase obtained by the HEBM aided sintering method.