Preparation and superconductivity of stoichiometric β-FeSe

Yujuan Xia,Fuqiang Huang,Xiaomin Xie,Mianheng Jiang

DOI: https://doi.org/10.1209/0295-5075/86/37008

2009-01-01

Abstract:The stoichiometric beta-FeSe superconductor was prepared for the first time by mechanical alloying (MA) from elemental powders of iron and selenium (1 : 1) and subsequent annealing process. The formation of the stoichiometric beta-FeSe is attributed to the MA resulting nanometric precursor containing high reaction activity for the following annealing process, and the MA mechanism here is a mechanic collision reaction (MCR). The crystalline phases in the MA precursor are tightly related to the milling time (t). Hexagonal gamma-Fe(7)Se(8), tetragonal beta-FeSe, and residual Fe coexist when t <= 5h. A single delta-FeSe phase is observed when t = 10h, and the crystalline size further decreases to similar to 10 nm. In the nanocrystalline state, hexagonal delta-FeSe is the stable and preferred phase. With the increase of the annealing temperature, d-FeSe rapidly transforms to the well-crystallized beta-FeSe. At 400 degrees C, the pure stoichiometric beta-FeSe phase is successfully obtained with size of similar to 60 nm and the highest superconductor transition temperature T(c)(onset) of about 8.9K in the beta-FeSe(1-x) series. Copyright (C) EPLA, 2009