Effect of ball milling on the phase constitution and microstructure of induction melted Higher Manganese Silicides and their thermoelectric properties

A. J. Zhou,X. B. Zhao,T. J. Zhu,E. Mueller,C. Stiewe,R. Hassdorf

2008-01-01

Abstract:Pellets of Higher Manganese Silicides (HMS) with a nominal composition of Mn15Si26 were fabri- cated by inductive levitation melting, followed by ball milling of different duration and hot pressing. The phase constitution and microstructure of the ball-milled powders and the hot-pressed pellets were investigated, and the Seebeck coefficient, the electrical and the thermal conductivity were measured from room temperature to 700 °C. It was found the ball milling process has introduced a phase transformation from HMS to MnSi (or Mn1- xFexSi), and the amount of Mn1-xFexSi increases with increasing ball milling energy and the milling duration. The average grain size was obviously decreased and reaches nano-scales after ball milling for more than 40 hours. The increasing amount of the Mn1-xFexSi phase has decreased the Seebeck coefficient, while increased the elec- trical and the thermal conductivity of the hot-pressed samples, thus deteriorated the thermoelectric performance of the material. The reasons for the phase transformation were discussed in this work with respect to the crystal structure of HMS and its stability under high-energy mechanical impact.