Effects of Ultrasonic Shot Peening and Multi-arc Ion Plating on Microstructure and Properties of TiAlN-Coated Cemented Carbide Materials
Xiaoxian Li,Shengjian Zhu,Huiming Chen,FuQian Tang,Xuehui Zhang,Tongxiang Liang
DOI: https://doi.org/10.1007/s11665-022-06740-5
IF: 2.3
2022-03-04
Journal of Materials Engineering and Performance
Abstract:The objective of this work was to evaluate the microstructure, mechanical properties, tribological performance, and corrosion behavior of TiAlN coatings prepared by the ultrasonic shot peening (USSP) pre-treatment of cemented carbide substrate and multi-arc ion plating (MAIP). The TiAlN coatings modified by USSP+MAIP combined surface treatment exhibited the preferred (111) crystal orientation of TiN. The intensity of the TiAlN diffraction peak was lower than that of the TiAlN coating without the USSP pre-treatment. At the same time, the interface of the TiAlN coating after the combined USSP+MAIP surface modification became thicker, the film thickness increased, and the grain size was refined. Compared with the TiAlN coating without the USSP pre-treatment, microhardness and coating-substrate bonding force were significantly improved, having maximal values of 2554 HV0.05 and 38.58 N, respectively. Compared with the un-USSP TiAlN coating, the TiAlN coating modified by the combined USSP+MAIP surface treatment exhibited an abrasive wear mechanism and adhesive wear mechanism, revealing better tribological properties. The electrochemical results showed that the TiAlN coating modified by the combined surface treatment had a higher open-circuit potential, lower corrosion current density, and higher polarization resistance. Due to the increased film thickness and the higher structure density, the modified TiAlN coating exhibited better protection efficiency and higher charge transfer resistance.
materials science, multidisciplinary