Effect of Hf substitution Cu on glass-forming ability, mechanical properties and corrosion resistance of Ni-free Zr–Ti–Cu–Al bulk metallic glasses
Z.S. Jin,Y.J. Yang,Z.P. Zhang,X.Z. Ma,J.W. Lv,F.L. Wang,M.Z. Ma,X.Y. Zhang,R.P. Liu
DOI: https://doi.org/10.1016/j.jallcom.2019.07.240
IF: 6.2
2019-10-01
Journal of Alloys and Compounds
Abstract:<p>A series of Ni-free Zr<sub>55</sub>Ti<sub>3</sub>Hf<sub><em>x</em></sub>Cu<sub>32-<em>x</em></sub>Al<sub>10</sub> (<em>x</em> = 0, 1, 2, 3, 4, 5 at. %) bulk metallic glasses (BMGs) were developed by copper mold suction-casting. The effect of partially substituting Cu by Hf was investigated in terms of glass-forming ability (GFA), mechanical properties, and corrosion behavior. As a result of the partial substitution, the GFA of Hf-bearing amorphous alloys were significantly enhanced as compared to Zr<sub>55</sub>Ti<sub>3</sub>Cu<sub>32</sub>Al<sub>10</sub> BMGs. Hf addition also enlarged the supercooled liquid region from 55 K to 70 K. The critical diameter was found to increase from 4 mm to 8 mm for <em>x</em> = 3. The corresponding compressive yield strength was over 1800 ± 21 MPa with a large plastic strain above 2.60 ± 0.10%. Electrochemical tests indicated that the lowest corrosion current density was 1.6 ± 0.1 × 10<sup>−8</sup> A/cm<sup>2</sup> for the alloy with <em>x</em> = 5 in H<sub>2</sub>SO<sub>4</sub> solution, thereby yielding a superior corrosion resistance.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering