Zero-Charged Catanionic Lamellar Liquid Crystals Doped With Fullerene C60 For Potential Applications In Tribology

Mengjun Chen,Baoyong Liu,Xiaolin Wang,Yanxu Fu,Jingcheng Hao,Hongguang Li
DOI: https://doi.org/10.1039/c7sm00800g
IF: 4.046
2017-01-01
Soft Matter
Abstract:The formation of lamellar liquid crystals (LLCs) has been demonstrated in a few salt-free catanionic surfactant systems and their properties have been well documented. However, examples of their combination with other materials are relatively rare. Herein, a salt-free zero-charged catanionic surfactant with low chain melting temperature was prepared by mixing equimolar tetradecyltrimethylammonium oxide (TTAOH) and oleic acid (OA) in water, and its concentration-dependent aggregate transition was investigated. In the dilute region (cTTAO <= 5 wt%), fluorescence microscopy observations revealed the formation of vesicles (the Lav phase). Further increasing cTTAO induced a transition from the Lav phase to LLCs via a region where vesicles and lamellae coexist. With ordered hydrophobic domains, the LLCs can be used as hosts for the doping of fullerene C-60 (refers to C-60 hereafter) with the highest C-60/TTAO weight ratio of 0.04. The doping of C-60 effectively improves the viscoelasticity of the LLCs confirmed by rheological characterization while only slight modifications on their matrixes have been detected using small angle X-ray scattering measurements. The LLC/C-60 hybrids with cTTAO = 80 wt% were then subjected to tribological measurements, and an obvious reduction in their friction coefficients and wear volumes was observed. The C-60/TTAO weight ratio at which the best tribological performance appears was determined to be 0.01. Our results indicate that the combination of C-60 and catanionic LLCs could lead to the appearance of a new generation of environmentally-benign lubricants.
What problem does this paper attempt to address?