Abstract:Tribofilm configuration under the boundary lubrication region is an essential concern to gain insight into the tribological enhancement of the two-dimensional (2D) nano materials toward base oils. In this work, several alkyl carboxylic acids modified 2D triazine-based covalent organic frameworks (ATC) nano platelets were fabricated and served as lubrication additives. When carbon atoms add up to 16, the best lubricating performance is exhibited at an additive concentration of 0.05 wt % and the friction coefficient and wear volume are, respectively, reduced by 56.0% and 89.6% as compared to those of pure PAO 10 base oil. The analysis of the focused ion beam-transmission electron microscope (FIB-TEM) on the worn surface reveals that an alternately multilayer tribofilm consisting of 2D platelet additives and oxides and/or metallic soap salts is formed on the frictional interface of steel substrate, with a well-ordered arrangement along the sliding direction, which dominates the contributions of the excellent lubrication.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c00614?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c00614</a>.Figures of optical photos, SEM images, AFM image, height profile, XPS spectra, size distribution as function of intensity, evolution of the friction of the coefficient of ATC blends, evolution of the electric contact resistance of ATC blends, magnification profiles, HRTEM image, and electron diffraction pattern and table of areal peak ratio of C═N/O vs C—C components of all ATC samples (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c00614/suppl_file/am1c00614_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Microtribologic Properties of A Covalently Attached Nanostructured Self-Assembly Film Fabricated from Fullerene Carboxylic Acid and Diazoresin

Microtribological Properties of a Novel C60-containing Self-Assembled Film

NANOTRIBOLOGICAL BEHAVIORS OF SELF-ASSEMBLED FULLERENE FILM

Studies of Mocrotribological Property on the Self-assembly Films from Diazoresin and C60-containing Polyelectrolyte

Self-Assembly and Tribological Property of a Novel 3-Layer Organic Film on Silicon Wafer with Polydopamine Coating as the Interlayer

THE SELF-ASSEMBLY THIN FILMS FROM WATER-SOLUABLE C60-CONTAINING POLYELECTROLYTES:SYNTHESIS,FABRICATION,AFM/FFM STUDIES

Characterization and Tribological Behavior of Octadecene, Dodecene and Undecenoic Acid Films on Si Substrate

Fabrication And Afm/Ffm Studies Of C-60-Containing Polyelectrolyte Self-Assembled Films

Preparation and Tribological Behaviors of an Amide-Containing Stratified Self-Assembled Monolayers on Silicon Surface

Fullerene-like Nanostructure Induced Excellent Friction Behavior in High Vacuum Environment for Hydrogenated Carbon Film

MICROTRIBOLOGICAL PROPERTY OF SELF-ASSEMBLY MULTILAYER FILMS BASED ON PAMAM DENDRIMERS

Fabrication of a thin film containing C60 derivative nanodomains by photo- polymerization of diacetylene acid

Surface Force Apparatus (Sfa) Studies Of Frictional Properties Of C-60 Copolymer Films

Multilayer Tribofilm: An Unique Structure to Strengthen Interface Tribological Behaviors

Novel C-60-Containing Ultra-Thin Film Based on Diazoresin

Observations of the Topography and Friction Properties of Macromolecular Thin Films at the Nanometer Scale

Structure and Microtribological Behavior of Teflon and Teflon/Si3N4 Micro-Assembling Film

Self-assembled Multilayer Films Based on Diazoresins Studied by Atomic Force Microscopy/friction Force Microscopy

High Loading Capacity and Wear Resistance of Graphene Oxide/Organic Molecule Assembled Multilayer Film

Tribological Properties Of Self-Assembled Monolayers

Structure, Properties and Growth Mechanism of a Self-Assembled Nanocylindrical MoS2/Mo-S-C Composite Film