Abstract:To increase the maximum internal pressure that a polyethylene (PE) pipe can withstand, a novel rotational shear system (RSS) was constructed in this study to fabricate PE pipes with enhanced hoop strength by applying hoop shear on the pipes using a rotational mandrel. The microstructure and morphology with the influences of melt plasticizing temperature on PE pipes processing under rotational shear were investigated indirectly using small-angle X-ray scattering and wide-angle X-ray diffraction (SAXS/WAXD) measurements. In the SAXS patterns, equatorial streaks and meridional scattering peaks were clearly observed in all three samples prepared at different melt plasticizing temperatures, 215, 235, and 255 °C. Their presence indicated that shish–kebab crystals form in rotational shear. Compared to those at the low melt temperature, the increase in the melt temperature enhanced the amount and the dimensions of shish formed. However, the shish also relaxed faster at the high melt temperature. This behavior was attributed to the enhancement of the molecular chain's athletic ability. The hoop tensile strength and the heat resistance of the pipes peaked at the melt plasticizing temperature of 235 °C, 75.2 MPa, 102.4 °C, up 1 MPa, 0.2 °C (compared to the 215 °C) and 7.8 MPa, 3.2 °C (compared to the 255 °C). The axial strength increased with an increase of melt plasticizing temperature. However, the increase of melt plasticizing temperature worsens the inherent good tensile toughness of PE100 pipes as the axial elongation at break decreases.This article has not yet been cited by other publications.

The effect of high-temperature annealing on thermal properties and morphology of polyethylene pipes prepared by rotational shear

The effect of annealing time on morphology, mechanical properties, and thermal conductivity of HDPE pipes produced by rotational shear

Enhanced effect of thermal expansion process in rotational shear technology for high performance HDPE pipes

Role of Melt Plasticizing Temperature in Morphology and Properties of PE100 Pipes Prepared by a Rotational Shear System

The Role of Mold Temperature on Morphology and Mechanical Properties of PE Pipe Produced by Rotational Shear

The role of mandrel rotation speed on morphology and mechanical properties of polyethylene pipes produced by rotational shear

Effect of Different Shear Modes on Morphology and Mechanical Properties of Polypropylene Pipes Produced by Rotational Shear

Effect of Annealing on the Microstructure and Mechanical Properties of Polypropylene with Oriented Shish‐kebab Structure

Effect of Die Temperature on Morphology and Performance of Polyethylene Pipe Prepared Via Mandrel Rotation Extrusion

Effect of Rotating and Drawing Speeds on the Structure and Properties of Polyethylene Pipes Prepared by Rotation Extrusion

Effect of annular expansion pipe extruder head on mechanical properties of pipes

Effect of the inner wall cooling rate on the structure and properties of a polyethylene pipe extruded at a high rotation speed

Effect of mandrel rotation speed on morphology and mechanical properties of polypropylene pipes produced by rotational shear

Effect of rotation extrusion and molecular weight on ductile failure of polyethylene pipes under hydrostatic pressure

Role of Ultrahigh Molecular Weight Polyethylene During Rotation Extrusion of Polyethylene Pipe

The Influence of the Annealing on the Slow Crack Growth Properties in Polyethylene Pipe

Effect of β nucleating agent and rotational shear on morphology and mechanical properties of polypropylene pipes

Highly Endurable Hydrostatic Pressure Polyethylene Pipe Prepared by the Combination of Rotation Extrusion and Lightly Cross-Linked Polyethylene

Effects of Annealing on the Hierarchical Crystalline Structures and Mechanical Properties of Injection‐molded Bars of High‐density Polyethylene

Effect of Annealing on Microstructure and Mechanical Properties of Polypropylene Random Copolymer

Thermally Conductive Study of Polyethylene/Al2O3Composite Networks Cross-linked Pipes by Electron Beam Irradiation