Exploring novel PVD coated wiper inserts' chip breaker designs and feed rates on tool wear and in-depth hole integrity of Ti-6Al-4V alloy when drilling in a dry environment
Muhammad Zubair Afzal,Sarmad Ali Khan,Syed Farhan Raza,Rakhshanda Naveed,Saqib Anwar,Muhammad Umar Farooq
DOI: https://doi.org/10.1016/j.jmapro.2024.09.097
IF: 5.684
2024-10-11
Journal of Manufacturing Processes
Abstract:Drilling of Ti-6Al-4V poses significant challenges, including rapid tool wear, elevated cutting temperatures, and chip formation difficulties. Previous studies have reported the use of solid carbide drills, and data on dry drilling is limited. In this study, a novel combination of wiper inserts fixed at the outer periphery and stepped inserts provided at the central location are used while drilling Ti-6Al-4V alloy without coolant. Various chip breaker designs of peripheral wiper inserts, having different groove width, depth and back wall slope, imparted on wiper inserts abbreviated as GR, LM and GT with different feed rates are used to evaluate the tool wear/life, wear mechanisms, surface roughness, surface damage, burr height at hole entry and exit points, and microhardness of the machined surfaces. Utilization of the LM geometry resulted in a significant rise in the quantity of drilled holes, as it facilitated the generation of shorter chips. A maximum of 117 holes are drilled using the LM geometry which is operated at 0.10 mm/rev feed rate with values of workpiece surface roughness varying between 0.70 and 0.90 μm. For all tests, the measured surface roughness is within 0.70 to 1.4 μm irrespective of geometry and feed rate. Upon examining the machine specimen using a scanning electron microscope (SEM), no voids or cracks are detected. However, scratch and feed marks are observed in tests conducted at lower feed rates, conversely, higher feed rate leads to plastic deformation/material side flow. The diametric error resulted in all the holes being oversized to a range of 20–100 μm. Material softening is observed, which is deepened to 400 μm beneath the cutting surface. The microhardness values of the machined material are observed to be 15 %–20 % less in comparison to the hardness of the bulk material. According to the findings of this study, a combination of LM geometry and 0.10 mm/rev feed rate is recommended with respect to best tool life and good hole integrity in dry cutting of Ti-6Al-4V alloy.
engineering, manufacturing