Abstract:Polyetherimide(PEI)/SiO2 composites were in situ prepared via sol-gel process in the presence of tetraethyl orthosilicate(TEOS) in a mixed solvent of N,N-Dimethylacetamide/tetrahydrofuran(DMAc/THF).Electronic microscopy was used to check dispersion quality in transmission mode and scanning mode,and the results showed that SiO2 particles could be uniformly dispersed in the composite under a certain amount(20 wt%) and the average size of the particles could be controlled within a compass of 80~300 nm.However,glomeration may occur if the concentration of SiO2 particles was beyond this range.Results of Differential scanning calorimetry(DSC) and thermogravimetric analysis(TGA) showed that the glass transition temperature(Tg) and decomposition temperature(Td) of PEI were improved by introducing SiO2 particles.The phase separation morphology of blends of 4,4′-diaminodiphenyl sulphone cured epoxy with PEI or PEI/SiO2composite was investigated by SEM and it showed that the introduction of SiO2 particles could reduce the size of the dispersion phase(PEI rich phase).Dynamic rheological measurement of epoxyresin(ER)/PEI/silica blends with different silica particle content was conducted at same isothermal temperature.The onset time of phase separation decreased as silica particles in the blend system increased because the silica particles could act as catalyst in the polymerization reaction and make the phase separation easier to occur.After that,the viscosity of system with higher particle concentration grew faster and made the phase separation process ends in an earlier stage.Dynamic mechanical thermal analysis(DMTA) and impact tests showed that using PEI/SiO2 as the modifier could enhance the modulus and toughness property of the epoxy resin system simultaneously.

Effect of Dimethy Diethoxysilane on TEOS Gelation Process

Spherical particles from tetraorthosilicate (TEOS) sol–gel process with dimethyldiethoxysilane (DDS) and diphenyldiethoxysilane (DPDS) addition

Synthesis, characterization and lubricating effect of long chain branched polydimethylsiloxane-g-polyethylene copolymers

Investigation of the Tetraethoxysilane‐derived Sol–gel Process by Rheological Oscillation Test and the Effect of Different Synthetic Parameters

Liquid-State Si-29 Nmr Investigation on Ammonia-Catalyzed Hydrolysis Kinetics of A Mixture of Tetraethoxysilane and Dimethyldiethoxysilane

Monomers effect on the gas and humid barrier properties in PECVD deposited SiOx film on PET surface

Size-Controllable Synthesis of Worm-Like Sio2 Microspheres Using Dodecylamine As Direct Agent in Ethanol/Water Solvent System

Pore size control of mesoporous silicas from mixtures of sodium silicate and TEOS

Sol-gel process kinetics for Si(OEt)4

Effect of the Monomer TEOS Flow Rate on the Formation of Silicon Dioxide Films by Nonequilibrium,atmospheric Pressure Plasma Jet

Hydrolysis and Condensation of Tetraethyl Orthosilicate at the Air–Aqueous Interface: Implications for Silica Nanoparticle Formation

FT‐IR Study of the Hydrolysis and Polymerization of Tetraethyl Orthosilicate and Polydimethyl Siloxane in the Presence of Tetrabutyl Orthotitanate

The Influence of Water Content on the Growth of the Hybrid-Silica Particles by Sol-Gel Method

Study of Sol–gel Reaction of Organically Modified Alkoxysilanes. Part I: Investigation of Hydrolysis and Polycondensation of Phenylaminomethyl Triethoxysilane and Tetraethoxysilane

Effect of TEOS on the rheological properties of polyvinylidene fluoride and poly(vinylidene fluoride-co-hexafluoropropylene)

Controlled Formation of Silica Particles from Tetraethyl Orthosilicate in Nonionic Water-in-Oil Microemulsions

Influence of synthesis parameters on the formation and structure of bimodal mesopore silica in a controlled sol-gel process

In Situ Preparation of Pei/Sio2 Composites and Their Modification for Epoxy Resin

A FT-IR Study of the Hydrolysis of Tetraethylorthosilicate (TEOS).

Preparation of Monodisperse Silica Particles with Controllable Size and Shape

Interaction of PEG with ionic surfactant SDS to form template for mesoporous material