Abstract:The wettabilities of molten metals on ceramics are poor normally. In order to improve the wettability, all existing ceramic brazing methods introduce a compound transition layer that is formed by the reaction of active metal and ceramic. The transition layer between brazing seam and ceramic however creates negative effect on the properties of brazing joints. This paper reports our study of the wetting effect of sputtered Al particles on AlN, which enables the direct brazing of AlN using deposited Al-based films as fillers, thereby eliminating the need of a transition layer. The results show that under the bombardment of energetic sputtered Al particles, Al-N chemical bonding is formed at the interface between Al film and AlN, which typically requires temperatures above 850 ℃, much higher than the melting point of Al. The bonding remained intact even after the Al film has been melted, achieving the wetting effect on AlN. As a result, the direct brazing of AlN without the need of a transition layer becomes feasible. The shear strength of Al/AlN joint using this process reaches 104 MPa. The addition of 3.8 at.% Cu to film fillers increases the shear strength to 165 MPa. The fracture is generated in metallic brazing seam in both cases. When Cu content increases to 9.1 at.%, the segregation of Cu at the interface between the brazing seam and the ceramic reduces the shear strength of the joint to 95 MPa. With Al-20 at.% Ge, the brazing temperature can be lowered to 510 ℃, although the segregation of Ge at interface results in a low shear strength of 48 MPa. Instead of the traditional use of molten metals, utilization of the metallic vapor particles to bombard AlN achieves the wetting and the direct brazing of ceramics, with no negative effect of transition layers. This breakthrough method provides a brand new perspective to the technique of ceramic brazing.

Ultrafast Ultrasonic-Assisted Joining of Bare Α-Alumina Ceramics Through Reaction Wetting by Aluminum Filler in Air

Microstructure and formation mechanism of Al2O3/Zn5Al/2024Al joint by ultrasonic assisted soldering process

Wetting and Oxidation During Ultrasonic Soldering of an Alumina Reinforced Aluminum–copper–magnesium (2024 Al) Matrix Composite

Direct welding of diffuse alumina ceramics by ultrashort pulse laser

Ultrasonic-assisted wetting and soldering of AlN ceramic by using a nonactive solder (Sn9Zn) in air

Realizing the Air Joining of ZrO2 Ceramics Through Al Metal

Realizing the air brazing of ZrO2 ceramics through Al metal

Ultrashort pulse laser welding of alumina ceramic and titanium

Interfacial Structure and Formation Mechanism of Ultrasonic-Assisted Brazed Joint of Sic Ceramics with Al-12si Filler Metals in Air

Sonocapillary and wetting mechanism during ultrasonic brazing porous Si3N4 ceramics in air

Alumina ceramics joined with screen-printed B2O3 by spark plasma sintering

Bonding mechanism in ultrasonic-assisted soldering of ZrO2 and 304 stainless steel using a micro-alloyed active solder alloy

Fabricating porous Si3N4 ceramics joint by ultrasonic brazing at 450 °C

Ultrasonic-assisted transient liquid phase bonding of SiC ceramic and aluminum alloy using an inactive Zn interlayer

Joining aluminum directly to aluminum nitride ceramics by a continuous-casting-bonding method

High-performance flash joining of MgAl2O4 transparent ceramics

Wetting and Brazing of Chromium Film-Deposited Alumina Using AgCu Filler Metal

"Wetting" and Brazing of Aln by Sputtered Al

Fundamental study on direct and serial joining of spherical alumina particles with CO 2 laser

A New Process for Bonding Al to Al2O3 Ceramics

Ultrafast ultrasonic-assisted transient liquid bonding Al/Mg in air