Abstract:Multi-layer crystallization and uncontrollable defects were the main factors that limiting the quality of Cu 2 ZnSn(S,Se) 4 (CZTSSe) films. Here a hybrid crystallization strategy was proposed to simultaneously improve the morphology and defect properties of CZTSSe film. Firstly, we found the variation of the microstructures (constitution, chemical environment of the elements, etc.) in precursor films can greatly alter the grain-growths of CZTSSe films. Detailed characterizations revealed that the chemical environment of S in the precursor film may influence the S-to-Se substitution of the film during the selenization process. This can further affect the grain-growth mechanism and the properties of CZTSSe film. While the S-to-Se substitution of the film mainly occurred below 500°C, the NaSe x on the surface of the film could dominate the grain-growth (Na-mechanism). For this mechanism, the CZTSSe film exhibited bi-layer morphology and relatively high band-tail energy, but shallow-acceptor was detected in the film. The solar cells based on the CZTSSe films reached the efficiency of 10.6%. As a comparison, liquid phase could be generated when the S-to-Se substitution of the film shifted to higher temperature (>500°C). In this condition, the grain-growth would be dominated by the liquid phase (LP-mechanism). Such mechanism can eliminate the multi-layer crystallization and reduce the band-tail energy, but the surface properties of the CZTSSe film was deteriorated and the formation of shallow-acceptor in CZTSSe was inhibited. The fabricated solar cells achieved the efficiency of 10.3%. Based on the results above, a bi-layer precursor film contained sub-layers with different microstructures was proposed to regulate the crystallization of CZTSSe. The co-existence of different microstructures in the precursor film could induce a hybrid grain-growth mechanism for the CZTSSe film (e.g., the Na-mechanism worked on the surface while the LP-mechanism worked in the bottom simultaneously). Such grain-growth mechanism can yield CZTSSe film with uniform morphology and favorable defect properties. The CZTSSe solar cells based on the hybrid grain-growth mechanism achieved the best efficiency of 12.6%. The investigation in this paper would provide new solutions for the crystallization regulation on CZTSSe photovoltaic material.

Optimized grain growth for efficient solution-processed Bi-doped Cu2ZnSn(S,Se)4 thin film solar cells via spin-coated layers adjustment and two-step selenization

Synthesis and Investigation of Solution-Processed Bi-doped Cu2ZnSn(S, Se)4 Thin-Film Solar Cells

Simultaneously improving the morphology and defect properties of CZTSSe film via hybrid grain-growth mechanism

Exploring the optimal two-step selenization process to enhance the performance of ionic liquid solution based Cu2ZnSn(S,Se)4 thin film solar cells

An Efficient Cr-doping Strategy to Optimize the Solution-Processed Cu2ZnSn(S,Se)4 Solar Cells for Better Optoelectronic Performance

Effects of Selenization Conditions on Microstructure Evolution in Solution Processed Cu2ZnSn(S,Se)(4) Solar Cells

Growth Mechanism and Properties of Nanostructure Cu2ZnSnSe4 Thin Films and Solar Cells

Growth Mechanism and Properties of Nanostructure Cu 2 ZnSnSe 4 Thin Films and Solar Cells

Realization of Grain Growth and Suppressed Bulk Defects for Efficient Solution-Processed Cu2ZnSn (S, Se)4 Solar Cells Via Co-Doping Strategy

Beyond 10% Efficient CZTSSe Thin-Film Solar Cells Fabricated by a Two-Step CdS Deposition Process

Segmented Control of Selenization Environment for High‐Quality Cu2ZnSn(S,Se)4 Films Toward Efficient Kesterite Solar Cells

Sb Doping Strategy to Promote Growth and Suppress Defects in Solution-Processed CZTSSe Solar Cells for Improved Optoelectronic Performance

Controllable Double Gradient Bandgap Strategy Enables High Efficiency Solution‐Processed Kesterite Solar Cells

Growth of Cu2znsnse4 Film under Controllable Se Vapor Composition and Impact of Low Cu Content on Solar Cell Efficiency

On the Growth Process of Cu2ZnSn(S,Se)4 Absorber Layer Formed by Selenizing Cu–ZnS–SnS Precursors and Its Photovoltaic Performance

Large-Grain Spanning Monolayer Cu2 ZnSnSe4 Thin-Film Solar Cells Grown from Metal Precursor

Enhancing the performance of CZTSSe solar cells via an alternate spin-coating process with DMSO and DMF

Growth of Large Grain-Size Cu2ZnSn(SxSe1-x)4 Thin Films by Annealing Precursors Sputtered from a Single Quaternary Target for Solar Cells Application

Realization of 11.5% Efficiency Cu2ZnSn(S,Se)4 Thin‐Film Solar Cells by Manipulating the Phase Structure of Precursor Films

High Efficiency Sb and Ag Double Doped Cu2ZnSn(S, Se)4 Thin Film Solar Cells Realized by Post-Heat Treatment Process of Heterojunction

Surprising Efficiency Enhancement of Cu 2 ZnSn(S,Se) 4 Solar Cells with Abnormal Zn/Sn Ratios