Abstract:The trade-off between strength and ductility remains a significant challenge for high-entropy alloys (HEAs). The layer-by-layer printing manner inherent in the laser powder bed fusion (L-PBF) leads to distinctive microstructures in alloys, in turn yielding unexpected performances that are promising for resolving this contradiction. At present, the influence of L-PBF technology on the microstructures and mechanical properties of near-eutectic HEAs has yet to be explored. In the present work, a metastable AlCo 0.4 CrFeNi 2.7 hypoeutectic HEA with an extraordinary strength-ductility combination was successfully fabricated using L-PBF. The precipitation behaviors and mechanical properties of the alloy were further modulated through annealing. The results reveal that the high cooling rates inherent in L-PBF promote the formation of a "pseudoeutectic" structure featuring the face-centered-cubic (FCC) + body-centered-cubic (BCC) dual-phase nanolamellae. Furthermore, after annealing at 600-750 °C, the L1 2 and B2 precipitates are generated in the FCC lamellae, accompanied by a coarsening of the original Cr-rich precipitates (BCC) in the BCC lamellae. The as-printed sample exhibits remarkable mechanical properties, posing a yield strength of 1007 MPa, an ultimate strength of 1249 MPa, and a total elongation of ∼25.1%. After annealing at 750 °C, the tensile yield strength and ultimate strength are further increased to 1201 MPa and 1512 MPa, respectively, while the elongation is maintained at ~15.1%. The analysis results demonstrate that the high strength originates from the hard BCC lamellae and nanolamellar interfaces, while the good ductility stems from the soft FCC lamellae and coordinated deformation of the dual-phase nanolamellae. Furthermore, the strength increase is further substantiated through the introduction of annealing-induced nanoprecipitates, thereby contributing to additional precipitation strengthening.

Effect of heat treatment on microstructure and mechanical properties of lightweight high-entropy alloy

Experimental and DFT Investigations of AlNbTiVZr High Entropy Alloys with Excellent Mechanical Properties

Microstructure evolution and mechanical behavior of a CoCrFeNiMn0.75Cu0.25 high-entropy alloy by thermo-mechanical treatment

Effect of Heat Treatment on the Microstructure and Mechanical Properties of the Al0.6CoCrFeNi High-Entropy Alloy

Selective laser melting of AlCoCrFeMnNi high entropy alloy: Effect of heat treatment

Effect of heat treatment on microstructure and mechanical properties of Al1.2CoCrFeNi2.1 high-entropy alloy fabricated by powder plasma arc additive manufacturing

The influence of heat treatment on microstructure and mechanical response of a newly developed non-equimolar AlCrCuFeNi high-entropy alloy: Experiments and numerical modeling

Exceptional strength-ductility synergy in additively manufactured (CoCrNi)90Al5Ti5 medium-entropy alloy by heat treatment

A new strategy to overcome the strength-ductility trade off of high entropy alloy

Progress in Light-weight High Entropy Alloys

Strength-ductility synergy of an additively manufactured metastable high-entropy alloy achieved by transformation-induced plasticity strengthening

A novel L1 2 -strengthened single crystal high entropy alloy with excellent high-temperature mechanical properties

Experimental research on mechanical performance of the lightweight composite slabs Research Progress on the Lightweight High-Entropy Alloys

Micromechanical origin for the wide range of strength-ductility trade-off in metastable high entropy alloys†

Overcoming strength-ductility tradeoff with high pressure thermal treatment

Mechanical behavior and microstructure-property correlation of a metastable interstitial high entropy alloy with hierarchical gradient structures

The Effect of Heat Treatment on the Microstructure and Mechanical Properties of Al0.6CoFeNi2V0.5 High Entropy Alloy

Microstructures and precipitation behaviors of a hypoeutectic high-entropy alloy prepared by laser powder bed fusion

Tailoring microstructures and mechanical properties of lightweight refractory Ti22Sc22Zr22Nb17V17 multi-phase high-entropy alloys by hot extrusion and annealing

Heat treatment effects on microstructure and mechanical properties of TiZrNbTa high-entropy alloy

Microstructure-Property Correlation and Its Evolution during Aging in an Al4.4Co26Cr19Fe18Ni27Ti5.6 High-Entropy Alloy