Abstract:The (TiB/Ti)-TiAl composites with a laminated structure composing of alternating TiB/Ti composite layers, α2-Ti3Al interfacial reaction layers of and γ-TiAl layers were successfully prepared by spark plasma sintering of alternately stacked TiB2/Ti powder layers and TiAl powder layers. And the influence of thickness ratio of TiB2/Ti powder layers to TiAl powder layers on microstructure evolution and mechanical properties of the resulting (TiB/Ti)-TiAl laminated composites were investigated systemically. The results showed that the thickening of α2-Ti3Al layers which originated from the reaction of Ti and TiAl was significantly hindered by introducing TiB2 particles into starting Ti powders. As the thickness ratio of TiB2/Ti powder layers to TiAl powder layers increased, the bending fracture strength and fracture toughness at room temperature of the final (TiB/Ti)-TiAl laminated composites were remarkably improved, especially for the (TiB/Ti)-TiAl composites prepared by TiB2/Ti powder layers with thickness of 800 μm and TiAl powder layers with thickness of 400 μm, whose fracture toughness and bending strength were up to 51.2 MPa·m1/2 and 1456 MPa, respectively, 293 % and 108 % higher than that of the monolithic TiAl alloys in the present work. This was attributed to the addition of high-performance network TiB/Ti composite layers. Moreover, it was noteworthy that the ultimate tensile strength at 700 °C of (TiB/Ti)-TiAl composites fabricated by 400 μm thick TiB2/Ti powder layers and 400 μm thick TiAl powder layers was as high as that at 550 °C of network TiB/Ti composites. This means the service temperature of (TiB/Ti)-TiAl laminated composites was likely raised by 150 °C, meanwhile a good combination of high strength and high toughness at ambient temperature could be maintained. Finally, the fracture mechanism of (TiB/Ti)-TiAl laminated composites was proposed.

A Cost-Efficient Fabrication Strategy for Conductive Ti2alc Honeycomb Monolith Using Elemental Powders

Fabrication and mechanical properties of three- dimensional enhanced TiAl/GH3536 hetero- honeycomb sandwich structure

Study on the Fabrication of Porous TiAl Alloy Via Non-Aqueous Gel Casting of a TiH2 and Al Powder Mixture

Slip casting and pressureless sintering of Ti3AlC2

Investigating phase transformation, densification and diffusion mechanism of TiH 2 powder to achieve a high ductile Ti6Al4V alloy

Fabrication and Compression Properties of Ti Honeycomb

Hierarchically heterogeneous strategy for Ti 2 AlC/TiAl composite with superior mechanical properties

Fabrication of Porous FeAl-based Intermetallics Via Thermal Explosion

Fabrication of Textured Ti2AlC Lamellar Composites with Improved Mechanical Properties

A possible mechanism on synthesis of Ti3AlC2

A Novel Fabrication Strategy for Highly Porous FeAl/Al2O3 Composite by Thermal Explosion in Vacuum

Fabrication of CaAl12O19‐CaTiO3 composites and their potential usage for TiAl alloy smelting

Achieving Superior High-Temperature Strength and Oxidation Resistance of TiAl Nanocomposite through In Situ Semicoherent MAX Phase Precipitation

Microstructure and Mechanical Properties of Ti2AlC Particle and In-Situ TiAl3 Reinforced Pure Al Composites

Fabrication and properties of Ti3AlC2-based ceramics by two-step method

Ti3alc2-Al2o3-Tial3 Composite Fabricated by Reactive Melt Infiltration

In-situ TiC/Ti composites based on Ti 2 AlC–Ti system: Reaction process, microstructure, and mechanical properties

Fabrication Of Tial Matrix Composite Sheetes With Controlled Micro-Laminated Architecture By A Solid-Liquid Reaction

Fabrication of (Tib/ti)-Tial Composites with a Controlled Laminated Architecture and Enhanced Mechanical Properties

Fabrication, microstructure and mechanical properties of TiAl matrix composite reinforced by submicro/nano-Ti 2 AlC

Porous TiAl alloys fabricated by sintering of TiH 2 and Al powder mixtures