Abstract:Titanium alloys can achieve ultrahigh strength through precipitation hardening of secondary alpha-phase (alpha s) from ,B-matrix but often compromise ductility due to the conventional strength-ductility trade-off. In this study, a new strategy based on ,B-subgrains-mediated hierarchical alpha-precipitation is devised to balance the conflict in Ti-6Al-2Mo-4Cr-2Fe (wt.%) alloy through a unique combination of hot rolling, short-term solid solution, and aging treatment, i.e., RSST + A. Tensile testing reveals that the RSST + A samples exhibit ultrahigh strength of similar to 1581 MPa and decent ductility of similar to 8.4 %, surpassing similar to 1060 MPa and similar to 2.7 % of the corresponding RSST counterparts without final aging treatment. This remarkable strengthening and counterintuitive ductilizing is attributed to the architecting of ,B-subgrains-mediated hierarchical alpha- precipitates as a result of our specific processing approach. The designed short-term solution introduces abundant ,B subgrains that are transformed from the retained intensive dislocations during hot rolling. The ,B subgrain boundaries subsequently promote a dramatic precipitation of alpha allotriomorphs (alpha GB) and Widmanst & auml;tten side-plates (alpha WGB), which effectively subdivides ,B grains into numerous tiny independent deformation units. Consequently, plastic strain is uniformly partitioned into a large number of small aged ,B subgrains during tension, which strongly impedes strain localization that would typically occur across multiple ,B subgrains in the fashion of long straight slip bands in the case of the RSST samples. Furthermore, the hierarchical alpha structure also postpones uncontrollable cracking even when structural damage occurs at the last stage of straining. These findings demonstrate that appropriately manipulating microstructure through elaborately designing processing routes enables unexpectedly ductilizing high- strength titanium alloys in the precipitation-hardening state. (c) 2024 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Enhancing Mechanical Properties of Tizralv by Engineering A Multi-Modal-Laminated Structure

Enhancing Ductility of Titanium Matrix Composites by Multimodal Α-Grains

Microstructure Regulation and Strength-Elongation Synergy of the Near Alpha TZAM Alloy Via Thermomechanical Processing

Enhanced Mechanical Properties of Ti-5Al-5Mo-5V-3Cr-1Zr by Bimodal Lamellar Precipitate Microstructures Via Two-Step Aging

A Hierarchical and Multiphase Nanolaminated Alloy with an Excellent Combination of Tensile Properties

Tailoring Microstructure and Tribological Properties of Cold Deformed Tizralv Alloy by Thermal Treatment

Microstructures and Tensile Properties of a High Strength Β Titanium Alloy Ti5Al4Zr8Mo7V by Near Β Forging and Β-Transus Forging

Heat-treatment induced microstructural evolution and enhanced mechanical property of selective laser melted near β Ti-5Al-5Mo-5 V-3Cr-1Zr alloy

Tensile Brittleness and Ductility Improvement in a Novel Metastable Β Titanium Alloy with Lamella Structure

Enhanced yield strength by fine grain strengthening and TRIP/TWIP effect of metastable β-type Ti-4V-2Mo-2Fe alloy with high ductility

A hierarchical nanolamella-structured alloy with excellent combinations of tensile properties

Achieving Synergy Between Strength and Ductility in Metastable Β-Titanium Alloy Through a Novel Multi-Morphological Microstructure

Microstructure evolution and mechanical properties of deformed TiZrAlV upon annealing

High-strength and thermally stable TiB2-modified Al–Mn–Mg–Er–Zr alloy fabricated via selective laser melting

Design of Metastable Β-Ti Alloys with Enhanced Mechanical Properties by Coupling Αs Precipitation Strengthening and TRIP Effect

Achieving High Strength and Ductility of a Metastable Β-Titanium Alloy Via Coupling Thermomechanical Processing and Heat Treatments

Breaking the high-temperature strength-ductility trade-off in TiAl alloys through microstructural optimization

Enhancing Strength-Ductility Synergy in Metastable Β-Ti Alloys Through Β-Subgrains-mediated Hierarchical Α-Precipitation

Achieving super-high strength and acceptable plasticity for a near β-type Ti-4.5Mo-5.1Al-1.8Zr-1.1Sn-2.5Cr-2.9Zn alloy through manipulating hierarchical microstructure

Microstructural dependence of strength and ductility in a novel high strength β titanium alloy with Bi-modal structure

Thermomechanical Processing of a Near-α Ti Matrix Composite Reinforced by TiBw